应用三元扩散偶技术测定了Ni-Cr-Mo三元系1358 K的等温截面,借助电子探针微区成分分析方法分析了Ni-Cr-Mo三元扩散偶的相区成分,并对其相关系进行了研究.测得Ni-Cr-Mo三元扩散偶在1358 K下存在一个中间化合物NiMo,Cr和Mo在扩散偶中形成连续固溶体,Ni和(Cr,Mo)有限固溶,扩散偶中未发现三元中间化合物.实验发现Ni-Cr-Mo三元系1358 K的等温截面存在一个三相区:Ni+NiMo+(Cr,Mo).
参考文献
[1] | David F;Hans F .[J].Journal of The Minerals,Metals & Materials Society,1999,51(01):14. |
[2] | 赵双群,张麦仓,董建新,谢锡善.新型高温合金700℃时效组织及力学性能[J].稀有金属材料与工程,2003(12):991-994. |
[3] | Dyme K S;Dollar M;Klrstrom D L .[J].Scripta Metallurgica et Materialia,1991,25(04):865. |
[4] | Zhao J C;Jzckson M R et al.[J].MRS Bulletin,2002,4:324. |
[5] | Venkatraman M;Neumann J P .[J].Bulletin of Alloy Phase Diagrams,1987,8(03):216. |
[6] | Brewer L .[J].Bulletin of Alloy Phase Diagrams,1989,10(4a):416. |
[7] | Brewer L .[J].Bulletin of Alloy Phase Diagrams,1988,9(02):99. |
[8] | Neumann J P .[J].Bulletin of Alloy Phase Diagrams,1989,10(01):5. |
[9] | Swaminathan S;Jacob K T .[J].Bulletin of Alloy Phase Diagrams,1989,10(04):329. |
[10] | Nash P .[J].Bulletin of Alloy Phase Diagrams,1986,7(05):466. |
[11] | Frisk K .[J].Claphad,1990,14(03):311. |
[12] | Singleton M F;Nash P.Phase Diagrams of Binary Nickel Alloys[M].Oh:ASM International,1991:207. |
[13] | Cui Yuwen;Lu Xiaogang;Jin Zhanpeng .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1999,30A(11):2735. |
[14] | 梁敬魁.相图与相结构[M].北京:科学技术出版社,1993 |
[15] | 金展鹏 .[J].中南工业大学学报(自然科学版),1984,1:27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%