研究了含Al量不同的HK40合金在工业纯Ar气氛中的高温抗氧化性能，用SEM、XRD等方法检查了氧化膜的形貌、结构与成分．结果表明，加入铝后合金表面在高温下形成均匀的Al2O3膜，从而提高了合金的高温抗氧化性能；Al加入量为6mass％时，合金的高温抗氧化性能最好．在1100℃时加Al的合金氧化增重遵从抛物线规律，且随Al含量的增加，抗氧化性能显著增强．随着合金中Al添加量的增加，高温氧化膜组成相（Cr2O3、CrMn1．5O4、MnCr2O4、Al2O3）中的Al2O3逐渐增加．同时Al的存在提高了表面氧化膜的均匀性，且氧化膜中的Fe、Ni含量远低于基体．
The high temperature oxidation resistance of HK40 alloys with different amount of Al in Ar atmosphere was investigated. The surface morphology and the phases in the oxide scale were analyzed using SEM and XRD, respectively. Experimental results indicated that after Al addition the formed Al2O3 scale on the alloy surface at high temperature was uniform, consequently improved the alloy oxidation resistance. The optimum high-temperature oxidation resistance was achieved with the addition of 6 mass% Al. The oxidation mass gains of the alloy complied with a parabolic law at 1100 ℃, and oxidation resistance of the allotys was significantly improved with the increase of aluminum content. At high temperature, the formed oxide scales consisted of Cr2O3, CrMn1.5O4, MnCr2O4 and Al2O3, and the amount of Al2O3 in oxide scales increased with the increase of aluminum content, while the presence of aluminum improved the surface homogeneity of oxide scale, and the content of Fe, Ni elements of the oxide scale is much lower than that of the alloys.
参考文献
| [1] | Saunders S R J, Monteiro M, Rizzo F. The oxidation behavior of metals and alloys at high temperatures in atmospheres containing water vapour: A review[J]. Prog. Mater. Sci., 2008, 53: 775. |
| [2] | Stott F H, Wood G C, Stringer J, The influence of alloying elements on the development and maintenance of protective scales [J]. Oxid. Met., 1995, 44(1-2): 113. |
| [3] | Wang D Q, Shi Z Y. Aluminizing and oxidation treatment of 1Cr18Ni9 stainless steel [J]. Appl. Surf. Sci., 2004, 227(1-4): 255. |
| [4] | Liu Z Y, Gao W, Dahm K L, et al. Oxidation behavior of sputter-deposited Ni-Cr-Al micro-crystalline coatings [J]. Acta Mater., 1998, 46(5): 1691. |
| [5] | 黄志荣,孙启凤,罗小秋.HP40钢表面Al2O3薄膜制备及抑制结焦性能研究[J].材料工程,2008,2:18. |
| [6] | 喇培清,曾丽,刘致远等.Al对HP40合金显微组织的影响[J].铸造,2008,57(5):487. |
| [7] | Liu Z Y, La P Q, Zeng L. Effect of aluminum on microstructure of HP40 steel [J]. J. Iron Steel. Res. Int., 2007, 14 (1): 373. |
| [8] | 曾丽,喇培清,刘致远等.铝对HP40合金高温抗氧化性能的影响[J].钢铁研究学报,2009,21(6):53. |
| [9] | Wysiekierski A G, Fisher G, Schillmoller C M. Control coking for olefins plants [J]. Hydrocarbon Process., Int. Ed., 1999, 78 (1): 97. |
| [10] | 朱日彰,卢亚轩.耐热钢和高温合金[M].北京:化学工业出版社,1996:32. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%