Time-dependent Fatigue Crack Propagation (FCP) behaviors of five Ni-base superalloys were investigated at various temperatures under fatigue with various holding times and sustained loading conditions.The new concept of damage zone is defined and employed to evaluate the alloys' resistance to hold-time FCP.A special testing procedure is designed to get the maximum damage zone of the alloys.Udimet 720 and Waspaloy show shorter damage zones than alloys 706 and 718.The fractographical analyses show that the fracture surfaces of the specimens under hold-time fatigue conditions are mixtures with intergranular and transgranular modes.As the extension of holding time per cycle, the portion of intergranular fracture increases.The effects of loading stress intensity, temperature, holding time, alloy chemistry, and alloy microstructure on damage zone and the crack growth behaviors are studied.Hold-time usually increases the alloy's FCP rate, but there are few exemptions.For instance, the steady state hold-time FCP rate of Waspaloy at 760℃ is lower than that without hold-time.The beneficial effect of hold-time was attributed to the creep caused stress relaxation during the hold-time.

参考文献

[1] [OL].http://www.cranfield.ac.uk/sims/quality/damage_detection.htm
[2] L Garimella;P Liaw;D Klarstrom .[J].Journal of The Minerals,Metals & Materials Society,1997,49(07):67.
[3] T Sudershan;M Louthan Jr .[J].International Materials Reviews,1987,32:121.
[4] D.Davidson;J.Lankford .[J].International Materials Reviews,1992,37:45.
[5] P Paris;F Erdogan .[J].Journal of Basic Engineering,Transactions of the ASME,1963,85:528.
[6] J Lanteigne;J-P Bailon .[J].Metallurgical and Materials Transactions,1981,12A:459.
[7] B.Tomkins .[J].Philosophical Magazine,1968,18:1041.
[8] S D Antolovich;A Saxenta;G R Chanati 等.[J].Engineering Fracture Mechanics,1975,7:649.
[9] M Speidel;P·Sahm;M·Speidel.in High Temperature Materials in Gas Turbines[M].Elsevier; New York,1974:207.
[10] Y Oh;S Nam;J Hong .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000,31A:1761.
[11] S Lynch .[J].Acta Materialia,1988,36:2639.
[12] M Stroosnijder;V Guttmann;J H W de Wit 等.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1995,26A:2103.
[13] A McEvily;J L Velazquez .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,23A:2211.
[14] H Smith;D Michel .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1986,17A:370.
[15] I Vasatis;R Pelloux .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1985,16A:1515.
[16] L Korusiewicz .[J].Journal of Dong and M Kumosa Scripta Met Mat,1993,29:573.
[17] E Fleury;L Remy .[J].Materials Science and Engineering A,1993,A167:23.
[18] K M Chang .[J].Acta Met Sin,1996,9:467.
[19] K M Chang;GE CR .[R].D Report No,1989.
[20] T Anderson.Fracture Mechanics[M].CRC Press; Boca Raton,1994:230.
[21] H Riedel;J R Rice .[Z].ASTM STP,1980,700:112.
[22] K.M.Chang;M.F.Henry;M.G.Benz.[J].Journal of The Minerals,Metals & Materials Society:29.
[23] A Turnbull;E.R.de los Rios;R.B.Tait;C.Laurant J.S.Boabaid .Fatigue & Fract.of Eng[J].Materials and Structures,1998,21:1513.
[24] K M Chang;X Liu .[J].Materials Science and Engineering A,2001,A308:1.
[25] H Merrick;S Floreen .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1978,9A:231.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%