采用等离子烧蚀装置对ZrCP/W复合材料的烧蚀性能进行了研究.结果表明:ZrCP/W复合材料的线烧蚀率随ZrC含量和烧蚀时间的增加而增大.烧蚀后,在试样表面形成了烧蚀坑和熔融层,熔融层的厚度达到1 mm左右.在烧蚀过程中,烧蚀层中的物相发生了化学反应,并生成了新相.复合材料的主要烧蚀机制是以熔化烧蚀为主,兼有热化学烧蚀.
参考文献
| [1] | 宋桂明 .TiC<,p>/W及ZrC<,p>/W复合材料的组织性能与热震行为[D].哈尔滨工业大学,1999. |
| [2] | 王玉金 .ZrC<,p>/W复合材料的组织结构与抗热性能研究[D].哈尔滨工业大学,2002. |
| [3] | Dickerson MB;Wurm PJ;Schorr JR;Hoffman WP;Wapner PG;Sandhage KH .Near net-shape, ultra-high melting, recession-resistant ZrC/W-based rocket nozzle liners via the displacive compensation of porosity (DCP) method[J].Journal of Materials Science,2004(19):6005-6015. |
| [4] | Zhang SC;Hilmas GE;Fahrenholtz WG .Zirconium carbide-tungsten cermets prepared by In situ reaction sintering[J].Journal of the American Ceramic Society,2007(6):1930-1933. |
| [5] | Song GM.;Zhou Y.;Wang YJ. .Elevated temperature ablation resistance and thermophysical properties of tungsten matrix composites reinforced with ZrC particles[J].Journal of Materials Science,2001(19):4625-4631. |
| [6] | Wang Y J;Zhou Y;Song G M et al.[J].Journal of Materials Science and Technology,2003,19(02):167. |
| [7] | Kosolapova Ya T.Handbook of High Temperature Compounds:Properties Productions Applications[M].Washington,DC:Hemisphere publishing corporation,1990:509. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%