用化学氧化法制备导电聚苯胺(PANI)和聚邻甲苯胺(POT).借助FT-IR和UV-Vis等分析手段研究了两种导电聚合物在结构和性能上的差异.结果表明,聚邻甲苯胺中甲基的空间位阻效应远大于诱导效应和超共轭效应.空间位阻导致聚邻甲苯胺的分子链发生扭转,链间间距增加,电荷的链内扩散和链间跃迁变得困难,因此其导电性低于聚苯胺.此外,由于聚邻甲苯胺存在甲基的空间位阻效应,它的UV-Vis和FT-IR的部分吸收峰与聚苯胺相比发生紫移.
参考文献
| [1] | Hubert S;Pham M C;Le Dao H et al.[J].Synthetic Metals,2002,128:67-81. |
| [2] | Lindfors T;Ivaska A .[J].Journal of Electroanalytical Chemistry,2002,535:65-74. |
| [3] | Lindfors T;Ivaska A .[J].Journal of Electroanalytical Chemistry,2002,531:43-52. |
| [4] | Ding L L;Wang X W;Gregory R V .[J].Synthetic Metals,1999,104:73-78. |
| [5] | Dhanabalan A;Malmonge J A;Riul A Jr et al.[J].Thin Solid Films,1998,327-329:808-812. |
| [6] | Albuquerque J. E.;MattoSob L. H. C. .A simple method to estimate the oxidation state of polyanilines[J].Synthetic Metals,2000(1/2):19-22. |
| [7] | Roy B C;Gupta M D;Bhoumik L et al.[J].Synthetic Metals,2002,130:27-33. |
| [8] | Dimitriev O P .[J].Journal of Colloid and Interface Science,2001,235:380-382. |
| [9] | 王利祥;王佛松 .[J].高分子学报,1989,3:264-269. |
| [10] | 孙东豪,丁进青,张展屏.聚邻甲苯胺合成及性能研究[J].塑料工业,1999(01):3-6. |
| [11] | Josefowicz J Y;Avlyanov J K;MacDiarmid A G .[J].Thin Solid Films,2001,393:186-192. |
| [12] | 郭亚平,郭亚军,吕君英,谭秀民.替代Ti-Mn-钡铁氧体/聚邻甲苯胺复合微粒的合成与表征[J].功能材料,2004(z1):973-976. |
| [13] | 郭亚平,郭亚军,吕君英.聚苯胺/铁氧体复合颗粒的合成与表征[J].材料科学与工艺,2005(02):189-192. |
| [14] | 王利祥;王佛松 .[J].应用化学,1990,7(05):1-10. |
| [15] | Kilmartin P A;Wright G A .[J].Synthetic Metals,1999,104:145-156. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%