本文采用超音速火焰喷涂方法(HVOF)制备了NiCr-Cr3C2-BaF2·CaF2/NiCr-Cr3C2和NiCr-Cr3C2-BaF2·CaF2两种涂层,对两种涂层试样进行了热冲击试验,研究了涂层的抗热震性能,并探讨了涂层的热疲劳特性.结果表明:NiCr-Cr3C2-BaF2·CaF2/NiCr-Cr3C2涂层热震75次后仍保持表面平整,相同条件下的NiCr-Cr3C2-BaF2·CaF2涂层热震5次即剥落;NiCr-Cr3C2中间层的引入缓和了涂层内应力,阻碍了热疲劳裂纹形成和扩展.在热冲击试验中基体与中间层之间形成的扩散层可吸收裂纹尖端应力,阻止裂纹进一步失稳扩展.
参考文献
| [1] | Dellacorte C .The effect of counterface on the tribological performance of a high temperature solid lubricant composite from 25 to 650℃[J].Surface and Coatings Technology,1996,86-87:486-492. |
| [2] | Dellacorte C;Sliney H E .Composition optimization of self-lubricating chromium-carbide-based composite coatings for use to 760℃[J].ASLE TRANSACTIONS,1987,30:77-83. |
| [3] | Fellenstein J A;Dellacorte C .Preliminary Tuft Testing of Metallic Bristles Versus PS212,PS300 and HVOF300[R].NASA TM-107522,1998. |
| [4] | Derby J;England R .Tribopair Evaluations of Brush seal Applications[R].AIAA paper 92-3715,1992. |
| [5] | Fellenstein J A;DellaCorte C .High Temperature Brush Seal Tuft Testing of Metallic Bristles Versus Chrome Carbide[R].NASA TM-107238,AIAA paper 96-2908,1996. |
| [6] | 黄传兵,杜令忠,张伟刚,王璐,侯广库.三种热喷涂工艺制备NiCr/Cr_3C_2-BaF_2·CaF_2涂层的结构与性能[J].航空材料学报,2009(06):70-76. |
| [7] | 薛庆增,张佳平,马力,王威.超音速喷涂含氟化物涂层工艺研究[J].新技术新工艺,2010(07):80-83. |
| [8] | 张佳平 .超音速火焰喷涂含氟化物的碳化铬/镍铬涂层结构与性能[J].中国表面科学,2011,24(2):46-50. |
| [9] | 周长华;张孝彬 .热喷涂技术的现状和发展[J].材料科学与工程学报,1998,16(4):71-73. |
| [10] | 侯根良,王汉功,袁晓静,苏勋家.基于超音速火焰喷涂技术的冷喷涂技术实现与流场分析[J].材料科学与工程学报,2005(02):160-162. |
| [11] | 殷傲宇,邓畅光,肖来荣,张吉阜.超音速喷涂Cr3C2-25％NiCr涂层在砂粒-水环境下的磨损行为研究[J].热加工工艺,2012(20):129-133,137. |
| [12] | 张吉阜,邓畅光,刘敏,周克崧,邓春明.超音速火焰喷涂NiCr／Cr3C2-BaF2·CaF2层的结构与性能[J].材料保护,2012(08):14-17. |
| [13] | 张显程,徐滨士,王海斗,吴毅雄.功能梯度涂层热残余应力[J].机械工程学报,2006(01):18-22. |
| [14] | 胡浩炬,张建宇,齐红宇,李志永,费斌军.热循环作用下圆筒基体热障涂层的失效过程分析[J].材料科学与工程学报,2010(01):13-17,61. |
| [15] | 赵文华,沈岩,肖金生.ZrO2-NiCr/Al梯度涂层的抗热震性能研究[J].中国表面工程,2004(03):21-25. |