采用聚酯多元醇(PEA)和聚醚多元醇(PTMG)为混合软链段,考察了相同原料组成而不同制备方法对聚氨酯材料力学性能及动态行为的影响.方法一:将PEA和PTMG混合后制成预聚体,用扩链剂(MOCA)扩链后合成聚氨酯;方法二:将PEA和PTMG分别制成备预聚体,按照一定比例取出2种预聚体,再按各自的扩链系数加入MOCA,反应数分钟后将两者混合制备PEA/PTMG混合软链段聚氨酯.动态力学分析表明,不同制备方法对材料的耗能模量及玻璃化转变温度有较大影响,也证实了按照方法二制备的聚氨酯具有多微区结构.论文的研究模式对制备多种不同微区共存的聚氨酯是有益的.
参考文献
| [1] | Mondal S;Hu JL .Structural characterization and mass transfer properties of polyurethane block copolymer: influence of mixed soft segment block and crystal melting temperature[J].Polymer international,2006(9):1013-1020. |
| [2] | Rueda-Larraz, L;d'Arlas, BF;Tercjak, A;Ribes, A;Mondragon, I;Eceizaa, A .Synthesis and microstructure-mechanical property relationships of segmented polyurethanes based on a PCL-PTHF-PCL block copolymer as soft segment[J].European Polymer Journal,2009(7):2096-2109. |
| [3] | Cristina Prisacariu;Elena Scortanu;Bogdan Agapie .THE EFFECT OF HARD SEQUENCE ORDERING ON THE MECHANICAL BEHAVIOR OF POLYURETHANE ELASTOMERS[J].International Journal of Polymer Analysis and Characterization,2012(1/8):312-320. |
| [4] | 吕志平,姚丽,毕晓霞,窦涛.多交联体系聚氨酯材料的制备与表征[J].高分子材料科学与工程,2008(09):147-150. |
| [5] | 杨茹果,李小宁,吕志平,杨云飞.多交联型聚氨酯材料的制备与性能[J].高分子材料科学与工程,2012(04):129-132. |
| [6] | Zhiping Lv;Xiaoning Li;Xiang Yu .The effect of chain extension method on the properties of polyurethane/SiO_2 composites[J].Materials & design,2012(Mar.):358-362. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%