采用金相分析、电子背散射衍射(EBSD)技术等方法研究了00Cr20Al6铁素体不锈钢在不同退火保温时间下其显微组织、再结晶比例及力学性能的变化.结果表明:当退火温度均为700℃时,随着退火后保温时间的延长,此钢的再结晶比例从66.4％升至94.3％,小角度晶界逐渐被大角度晶界所替代,伸长率从15％升高至22.7％.经对比,当退火温度在700℃,保温时间为20 min时,此钢获得了较好的综合力学性能.
参考文献
| [1] | 张文华.不锈钢及其热处理[M].沈阳:辽宁科学技术出版社,2010 |
| [2] | 肖益鸿,蔡国辉,詹瑛瑛,魏可镁.汽车尾气催化净化技术发展动向[J].中国有色金属学报,2004(z1):347-353. |
| [3] | 沈黎明;陆建生.汽车尾气净化器载体研究综述[J].上海钢研,2004(01):35-41. |
| [4] | 杨连宏,李龙蛟,刘雅政,周乐育.430铁素体不锈钢的热变形行为[J].金属热处理,2011(12):78-82. |
| [5] | Xiang Chen;Rick Haasch et al.Impedance spectroscopy and microstructure charaterization of the corrosion behavior of FeCrAl alloy in lead-bismuth eutectic[J].Journal of Nuclear Materials,2012,431(1-3):125-132. |
| [6] | D. J. Young;A. Chyrkin;W. J. Quadakkers .A Simple Expression for Predicting the Oxidation Limited Life of Thin Components Manufactured from FCC High Temperature Alloys[J].Oxidation of Metals,2012(5/6):253-264. |
| [7] | Chi Zhang;Zhenyu Liu;Guodong Wang .Effects of hot rolled shear bands on formability and surface ridging of an ultra purified 21%Cr ferritic stainless steel[J].Journal of Materials Processing Technology,2011(6):1051-1059. |
| [8] | 吕卫东,高飞,刘振宇,王国栋.B对Nb稳定化的超纯Cr17铁素体不锈钢性能的影响[J].金属热处理,2011(08):55-58. |
| [9] | 李亚波,王福明,尚成嘉,李长荣.铈对低铬铁素体不锈钢静态再结晶行为的影响[J].材料热处理学报,2010(03):64-68. |
| [10] | 刘海涛,孙宇,刘振宇,王国栋.热轧工艺对超纯Cr17铁素体不锈钢成形性能的影响[J].材料热处理学报,2011(05):46-50. |
| [11] | 毛为民;赵新兵.金属的再结晶与晶粒长大[M].北京:冶金工业出版社,1994 |
| [12] | 申林远,孙蓟泉,苏岚,王立军.冷轧压下率和退火工艺对超低碳IF钢再结晶及力学性能的影响[J].机械工程材料,2011(09):1-4,10. |
| [13] | Haitao Yan;Hongyun Bi;Xin Li .Microstructure and texture of Nb+Ti stabilized ferritic stainless steel[J].Materials Characterization,2008(12):1741-1746. |
| [14] | 杜伟,江来珠,孙全社,刘振宇.冷轧压下率对铁素体不锈钢深冲性能的影响[J].材料热处理学报,2010(08):61-65. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%