采用显微硬度与电导率测试、拉伸试验、晶间腐蚀及剥落腐蚀试验、金相(0M)及扫描电镜(SEM)观察,研究了热处理制度对含Sr Al-7.0Zn-1.4Mg-1.5Cu-0.14Zr 7085铝合金挤压材性能的影响.结果表明:固溶处理对合金的拉伸性能影响显著,强化固溶合金强度要明显高于常规固溶合金,常规固溶(470℃×2 h)T76(121℃×5 h +153℃×16 h)时效处理合金的屈服强度与抗拉强度分别为436.8 MPa、492.25 MPa,而经强化固溶(470℃×2 h+480℃×2 h+490℃ ×2 h)T76处理的合金为471.8MPa、518.25 MPa;时效制度对合金的硬度、电导率及抗腐蚀性能有较大影响,T76(121℃×5 h+153℃×16h)时效处理后,合金获得较好的性能配合.本合金的最佳热处理制度为强化固溶T76时效处理,此时合金具有良好的综合性能.
参考文献
| [1] | T. Warner .Recently-Developed Aluminum Solutions for Aerospace Applications[J].Materials Science Forum,2006(Pt.2):1271-1278. |
| [2] | Dixit M;Mishra RS;Sankaran KK .Structure-property correlations in Al 7050 and Al 7055 high-strength aluminum alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):163-172. |
| [3] | 曹春晓.一代材料技术,一代大型飞机[J].航空学报,2008(03):701-706. |
| [4] | Amjad Saleh El-Amoush .Investigation of corrosion behaviour of hydrogenated 7075-T6 aluminum alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):171-177. |
| [5] | Olivera A F Jr;de Barros M C et al.The effect of RRA on the strength and SCC resistance on AA7050 and AA7150 aluminium alloy[J].Materials Science and Engineering A,2004,379(1-2):321-326. |
| [6] | 许晓静,吴桂潮,王彬,张福豹,罗勇,宋涛,成城,潘励,程晓农.含Sr7085型铝合金的晶间腐蚀和剥落腐蚀性能[J].材料热处理学报,2011(05):22-26. |
| [7] | GB/T228-2002.金属材料室温拉伸试验方法[S].,2002. |
| [8] | GB 7998-2005.铝合金晶间腐蚀测定方法[S].,2005. |
| [9] | ASTM G110-1992 (1997.Standard practice for evaluating intergranular corrosion resistance of heat treatable aluminum alloys by immersion in sodium chloride + hydrogen peroxide solution[S].,1997. |
| [10] | GB/T 22639-2008.铝合金加工产品的剥落腐蚀试验方法[S].,2008. |
| [11] | ASTM G34-2001.Standard test method for exfoliation corrosion susceptibility in 2XXX and 7XXX series aluminum alloys (EXCO test)[S].,2001. |
| [12] | 陈康华,刘允中,刘红卫.7075和2024铝合金的固溶组织与力学性能[J].中国有色金属学报,2000(06):819. |
| [13] | 戴晓元,夏长清,孙振起,华熳煜,Long Chunguang.强化固溶对Al-7.6Zn-2.1Mg-1.30Cu-0.15Zr-0.30Sc合金组织与性能的影响[J].稀有金属材料与工程,2007(z3):195-198. |
| [14] | 李锡武,熊柏青,张永安,李志辉,朱宝宏,刘红伟.时效对新型Al-Zn-Mg-Cu合金力学及应力腐蚀性能的影响[J].稀有金属,2010(04):503-508. |
| [15] | P. GUYOT;L. COTTIGNIES .PRECIPITATION KINETICS, MECHANICAL STRENGTH AND ELECTRICAL CONDUCTIVITY OF AlZnMgCu ALLOYS[J].Acta materialia,1996(10):4161-4167. |
| [16] | M. J. Starink;S. C. Wang .A model for the yield strength of overaged Al-Zn-Mg-Cu alloys[J].Acta materialia,2003(17):5131-5150. |
| [17] | J.F. Li;Z.Q. Zheng;S.C. Li;W.J. Chen;W.D. Ren;X.S. Zhao .Simulation study on function mechanism of some precipitates in localized corrosion of Al alloys[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(6):2436-2449. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%