TiO2 thin films were prepared by DC magnetron sputtering with the oxygen flow rate higher than the threshold. The film deposited for 5 h was of anatase phase with a preferred orientation along the <220> direction, but the films deposited for 2 and 3 h were amorphous. The transmittance and photocatalytic activity of the TiO2 films increased constantly with increasing film thickness. When the annealing temperature was lower than 700℃, only anatase grew in the TiO2 film. TiO2 phase changed from anatase to rutile when the annealing temperature was above 800℃. The photocatalytic activity decreased with increasing annealing temperature.