采用溶胶-凝胶技术,以4,4'-(六氟异丙基)-苯二酸酐(6FDA)、5,5'-(六氟异丙基)-二-(2-氨基苯酚)(6FHP)、非线性生色分子4-(N-2-羟乙基-N-甲基氨)-4'-[(6-硝基苯并噻唑-2-取代)二氮烯基偶氮苯(HNBDA)、偶联剂γ-氨丙基三乙氧基硅烷(APTES)和正硅酸乙酯(TEOS)水解液合成了系列的聚酰亚胺/SiO2杂化材料,其中TEOS的含量为0~22.5%.采用红外、热分析、扫描电镜、透射电镜和X射线衍射等进行表征.它们的玻璃化转变温度和热分解温度分别为216~366℃和321~438℃,表明具有较好的热稳定性.测定极化后材料832nm处的电光系数γ33为21~35 pm/V,且电光系数保持其初始值的85%以上(100 h),结果表明杂化材料在光器件上具有潜在的应用.
A series of the polyimide-silica NLO hybdd materials were synthesized from 4,4'-(Hexafluoroisopropylidene)-diphthalic Anhydride(6FDA),2,2-Bis(3-amino-4-hydroxyphenyl)hexafluoropropane(6FHP),nonlinear optical (NLO)molecule 4-(N-2-Hydroxyethyl-N-methylamino)-4'-[(6-nitroben-zothiazol-2 yl)diazenyl]azobenzene(HNBDA),coupling agent APTES and hydrolysate of TEOS via sol-gel process.The TEOS content in the hybrid films was varied from 0 to 22.5wt%.The prepared polyimide/silica hybrids were characterized by IR,thermogravimetric analysis(TGA),scanning electron microscopy(SEM),Transmission Electron Microscope(TEM),X-ray diffraction(XRD)etc.The glass transition temperature(Tg)and the decomposition temperature(Td)were in the range 216~366℃and 321~438℃respectively for materials.These results show that these hybrid materials had an excellent thermal stability.The electro-optic coefficients(γ33)at the wavelength of 832 nm for polymer thin films poled were in the range of 21~35 pm/V and the values remained well (retained>85%for more than 100 h).The experimental results suggest that the hybrid thin films have potential applications as passive films for optical devices.
参考文献
[1] | Sigurd Schrader;Vismants Zauls;Birgit Dietzel;at al .[J].Materials Science and Engineering C,1999,8-9:527. |
[2] | Liu Li;Lu Qinghua;Yin Jie et al.[J].Materials Science and Engineering C,2002,22(01):61. |
[3] | Houbertz R.;Domann G.;Cronauer C.;Schmitt A.;Martin H.;Park JU. Frohlich L.;Buestrich R.;Popall M.;Streppel U.;Dannberg P.;Wachter C. Brauer A. .Inorganic-organic hybrid materials for application in optical devices[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2003(1/2):194-200. |
[4] | Chiang Pei-Chun;Whang Wha-Tzong .[J].Polymer,2003,44(08):2249. |
[5] | Qiu Fengxian;Zhou Yuming;Liu Juzheng et al.[J].Dyes and Pigments,2006,71(01):37. |
[6] | Ibanez A;Levy J P;Mouget C et al.[J].Journal of Solid State Chemistry,1997,129(01):22. |
[7] | Hiroaki Tachibana;Yasushi Yamanaks;Hideki Sakai et al.[J].Chemistry of Materials,2000,12(03):854. |
[8] | Mei-Hui Tsai;Wha-Tzong Whang .Low dielectric polyimide/poly(silsesquioxane)-like nanocomposite material[J].Polymer: The International Journal for the Science and Technology of Polymers,2001(9):4197-4207. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%