采用电化学阻抗谱(EIS)和傅里叶变换红外光谱(FTIR)等方法研究了干湿交替环境和全浸环境试验条件下,环氧厚涂底漆在3.5% NaCl溶液中的劣化过程和机制.在干湿交替和全浸两种条件下,涂层的劣化主要是由于涂层中环氧基团在电解质溶液中的水解.涂层中孔洞等缺陷及环氧基团水解生成的亲水性-OH,-NH2等基团,促进了电解液的渗透,加速了涂层的劣化进程.在干湿交替环境中,涂层劣化明显快于全浸环境.这是由于干湿交替环境中,涂层水解程度较全浸环境中更高,且干燥过程中氧的补充加速了阴极区的反应,促进了金属基体的腐蚀,使得涂层附着力变差.另外,在干湿交替循环作用下,由于涂层与基体涨缩不一致引起的内应力也加速了涂层的劣化过程.

参考文献

[1] A.P. Yadav;A. Nishikata;T. Tsuru .Electrochemical impedance study on galvanized steel corrosion under cyclic wet-dry conditions-influence of time of wetness[J].Corrosion Science,2004(1):169-181.
[2] Allahar KN;Hinderliter BR;Bierwagen GP;Tallman DE;Croll SG .Cyclic wet drying of an epoxy coating using an ionic liquid[J].Progress in Organic Coatings: An International Review Journal,2008(1):87-95.
[3] El-Mahdy GA.;Tsuru T.;Nishikata A. .Electrochemical corrosion monitoring of galvanized steel under cyclic wet-dry conditions[J].Corrosion Science,2000(1):183-194.
[4] Lendvay-Gyorik G;Pajkossy T;Lengyel B .Corrosion-protection properties of water-borne paint coatings as studied by electrochemical impedance spectroscopy and gravimetry[J].Progress in Organic Coatings: An International Review Journal,2006(4):304-310.
[5] J.H. Park;G.D. Lee;H. Ooshige;A. Nishikata;T. Tsuru .Monitoring of water uptake in organic coatings under cyclic wet-dry condition[J].Corrosion Science,2003(8):1881-1894.
[6] Lendvay-Gyorik G;Pajkossy T;Lengyel B .Corrosion-protection properties of water-borne paint coatings as studied by electrochemical impedance spectroscopy and gravimetry[J].Progress in Organic Coatings: An International Review Journal,2006(4):304-310.
[7] 张亮,唐聿明,左禹.氟碳涂层在干湿交替环境下失效过程研究[J].化工学报,2011(07):1977-1982.
[8] 谢德明,童少平,胡吉明,郑奕,王建明,张鉴清.多道富锌基涂层在NaCl溶液中的电化学行为研究[J].金属学报,2004(07):749-753.
[9] 赵增元,孔爱民,王佳,吕伟艳.浪花飞溅区和潮差区干湿循环对有机涂层失效影响研究[J].中国造船,2008(z2):326-331.
[10] 胡吉明,张鉴清,曹楚南.铝合金表面环氧涂层中水传输行为的电化学阻抗谱研究[J].金属学报,2003(05):544-549.
[11] 张颖怀,许立宁,路民旭,张璞.用电化学阻抗谱(EIS)研究环氧树脂涂层的防腐蚀性能[J].腐蚀与防护,2007(05):227-230,234.
[12] Perrin FX.;Aragon E.;Vernet JL.;Irigoyen M. .Artificial aging of acrylurethane and alkyd paints: a micro-ATR spectroscopic study[J].Polymer Degradation and Stability,2000(3):469-475.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%