制备了不同气氛下烧结的NiFe2O4陶瓷材料,研究了烧结气氛和烧结温度对NiFe2O4陶瓷物相组成、致密度、导电率和显微组织的影响.结果表明:NiFe2O4在N2气氛下烧结时,晶格发生部分畸变,但物相组成不发生改变;与空气条件下烧结过程相比,N2气氛在保证材料获得较高的致密度和导电率的同时,有效降低了烧结温度.NiFe2O4陶瓷在N2气氛中1250℃烧结时,致密度为93.20%,960℃下的导电率20.83S/cm,气孔率为6.80%,平均晶粒粒径为4～5μm.
参考文献
| [1] | 刘业翔.铝电解惰性阳极与可湿润性阴极的研究与开发进展[J].轻金属,2001(05):26-29. |
| [2] | Pawlek R P.Inert Anodes: An Update[A].Warrendale:TMS,2002:449-456. |
| [3] | Gray P T.Corrosion and Passivation of Cermet Inert Anodes in Cryolite-Type Electrolytes[A].Warrendale:TMS,1986:309-320. |
| [4] | Weyand J D;Ray S P;Tarcy G P et al.Inert Anodes for Aluminum Smelting[R].DOE/CS/40158-20,Washington D C:Aluminum company of America,1986. |
| [5] | 张雷,周科朝,李志友,张晓泳.气氛对NiFe2O4陶瓷烧结致密化的影响[J].中国有色金属学报,2004(06):1002-1006. |
| [6] | LI Jie;DUAN Hua-nan;LAI Yan-qing .Effect of NiO content on corrosion behaviour of Ni-a;NiO-NiFe_2 O_4 cermets in Na_3 AlF_6-Al_2 O_3 melts[J].Transactions of Nonferrous Metals Society of China,2004(6):1180-1186. |
| [7] | 秦庆伟,赖延清,张刚,田忠良,周新林,李劼,刘业翔,贺跃辉.铝电解惰性阳极用Ni-Zn铁氧体的固态合成[J].中国有色金属学报,2003(03):769-773. |
| [8] | 关振铎;张中太;焦金生.无机材料物理性能[M].北京:清华大学出版社,2002:212-213. |
| [9] | Lai Y Q;Li J;Liu Y X.An Improved Pyroconductivity Test of Spinel-Containing Cermet Inert Anodes in Aluminum Electrolysis Cells[A].Tabereaux A:Charlotte:TMS,2005:339-343. |
| [10] | Mazzoni A D .[J].Ceramics International,2000,26:147-151. |
| [11] | 刘维跃;刘雄光 .[J].天津大学学报,1996,29(05):721-726. |
| [12] | 顾峰,沈悦,郭敏,王树棠.气氛烧结对95氧化铝陶瓷机械性能的影响[J].上海大学学报(自然科学版),2000(05):395-398. |
| [13] | 果世驹.粉末烧结理论[M].北京:冶金工业出版社,1998:98-100. |
| [14] | 王正文,姚熹,张良莹.烧结气氛对CuO添加BiNbO4陶瓷[J].电子元件与材料,2003(12):7-9. |
| [15] | ElSayed A M .[J].Ceramics International,2002,28:651-655. |
| [16] | 顾秉林;王喜坤.固体物理学[M].北京:清华大学出版社,1989:286-288. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%