The influence of calcium treatment on non-metallic inclusions had been studied when control technology of refining top slag in ladle furnace was used in ultra-low oxygen steelmaking. A sufficient amount aluminium was added to experimental heats for final deoxidizing during BOF tapping, and the refining top slag with strong reducibility, high basicity and high Al2O3 in ladle furnace was used to produce ultra-low oxygen steel and the transformation of nonmetallic inclusions in molten steel was compared by calcium treatment and no calcium treatment. The results show that the transformation of Al2O3--MgO - Al2O3 spinel-CaO-MgO-Al2O3 complex inclusions has been completed for aluminum deoxidation products and calcium treatment to molten steel is unnecessary when using the control technology of ladle furnace refining top slag to produce ultra-low oxygen steel, and the complex inclusions are liquid at the temperature of steelmaking and easily removable to obtain very high cleanliness steel by flotation. Further- more, the problems of nozzle clogging in casting operations do not happen and the remaining oxide inclusions in steel are the relatively lower melting point complex inclusions.
参考文献
| [1] | Paul S K;Ray A .Influence of Inclusion Characteristics on the Formability and Toughness Properties of a Hot-Rolled Deep- Drawing Quality Steel[J].Journal of Materials Engineering and Performance,1997,6(01):27. |
| [2] | Hideaki SUITO;Ryo INOUE .Thermodynamics on Control of Inclusions Composition in Ultraclean Steels[J].ISIJ International,1996(5):528-536. |
| [3] | ZHANG Li-feng;Thomas B G;WANG Xin-hua.Evalu- ation and Control of Steel Cleanliness-Review[A].Warrendale Is.n.1,2002:431. |
| [4] | K. Taguchi;H. Ono-nakazato;T. Usui .Complex deoxidation equilibria of molten iron by aluminum and calcium[J].ISIJ International,2005(11):1572-1576. |
| [5] | Lifeng ZHANG;Brian G. THOMAS .State of the Art in Evaluation and Control of Steel Cleanliness[J].ISIJ International,2003(3):271-291. |
| [6] | Kyoko WASAI;Kusuhiro MUKAI;Akifumi MIYANAGA .Observation of Inclusion in Aluminum Deoxidized Iron[J].ISIJ International,2002(5):459-466. |
| [7] | Ryousuke TAKATA;Jian YANG;Mamoru KUWABARA .Characteristics of Inclusions Generated during Al-Mg Complex Deoxidation of Molten Steel[J].ISIJ International,2007(10):1379-1386. |
| [8] | Rakers K G;Thomas B G.Clogging in Continuous Casting Nozzles[A].War- rendale,1995 |
| [9] | L. Holappa;M. Hamalainen;M. Liukkonen .Thermodynamic examination of inclusion modification and precipitation from calcium treatment to solidified steel[J].Ironmaking & Steelmaking: Products and applications,2003(2):111-115. |
| [10] | Ye G;J6nsson P;Lund T .Thermodynamics and Kinetics of the Modification of A12Oa Inclusions[J].ISIJ International,1996,36(Supplement):S105. |
| [11] | Ozturk B;Turkdogan E T .Equilibrium Sulphur Distribution Between Molten Calcium Aluminate and Steel[J].Metal Sci- ence Journal,1984,18:299. |
| [12] | Lu D Z;Irons G A;Lu W K .Kinetics and Mechanisms of Calcium Dissolution and Modification of Oxide and Sulphide Inclusions in Steel[J].Ironmaking and Steelmaking,1994,21(05):362. |
| [13] | Inoue R;Suito H .Calcium Desulfurization Equilibrium in Liq- uid Iron[J].Steel Researeh International,1994,65:403. |
| [14] | S. K. CHOUDHARY;A. GHOSH .Thermodynamic Evaluation of Formation of Oxide-Sulfide Duplex Inclusions in Steel[J].ISIJ International,2008(11):1552-1559. |
| [15] | WANG Xin-hua;WANG Wan-jun;LI Hai-bo.Compo- sition Change of the Non-Metallic Inclusions During the Sec- ondary Refining of Low Oxygen Alloyed Structural Steels[A].Busan,2009:24. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%