对挤压法和＂连铸-冷轧＂法两种工艺生产的H65黄铜管的组织与性能进行了综合对比研究。结果表明：两种工艺下H65黄铜管成品平均晶粒尺寸相差较小,挤压法工艺约14μm,＂连铸-冷轧＂法工艺约18μm;＂连铸-冷轧＂法成品管抗拉强度为335MPa,伸长率为61%,硬度为84.7HV1.0,挤压法成品管分别为360MPa,67.5%和82.6HV1.0,均达国标要求;挤压法成品管平均偏心率约12.5%,而＂连铸-冷轧＂法成品管偏心率仅为6.2%,且综合成材率较挤压法提高了11%。分析表明,高效短流程的＂连铸-冷轧＂法H65黄铜管加工工艺具有良好的发展前景。
Microstructure and properties of H65 brass tubes which were manufactured by continuous casting and cold rolling（CCR） process and extrusion process were studied and compared comprehensively.The results show that H65 brass tubes manufactured through these processes have the similar grain size.Average grain size of products by extrusion process is about 14μm,while products by CCR process is about 18μm.Products of CCR process have great mechanical properties for its σb reaches 335MPa,δ approaches 61%,hardness is 84.7HV1.0,so as the product of extrusion process,the tensile strength,elongation and hardness reach 360 MPa,67.5% and 82.6HV1.0,respectively.They all have reached the national standard.Average eccentricity of product by extrusion process is 12.5%.However,the average eccentricity of products by CCR process is only 6.2%,its finished product rate increased by 11% compared with extrusion process.The CCR process of H65 brass manufacturing method with a short process and high efficiency has good prospects for development.
参考文献
| [1] | 肖寒 .TP2铜管坯水平连铸工艺缺陷研究[D].大连理工大学,2006. |
| [2] | 周文龙,许沂,张士宏,于传富,蒋强,张金利.铸轧法与挤压法生产TP2铜管组织和性能对比分析[J].锻压装备与制造技术,2004(01):34-37. |
| [3] | 郭莉.国内铜及铜合金管棒材生产技术与装备[J].铜合金,2010(01):21-24. |
| [4] | 王乐俊 .铜管生产的工艺及其特点[J].上海有色金属,1999,20(01):22-25. |
| [5] | 洪正军.铜盘管铸轧工艺论述[J].铜业工程,2004(03):23-25. |
| [6] | 何新宇.(a+β)黄铜的挤压工艺与质量控制[J].有色金属与稀土加工,1997(02):26-30. |
| [7] | 李宏磊;娄花芬;马可定.铜加工生产技术问答[M].北京:冶金工业出版社,2007:289-300. |
| [8] | Xintao Li;Zhaoxiang Guo;Xiangwei Zhao;Bi Wei;Fengbao Chen;Tingju Li .Continuous casting of copper tube billets under rotating electromagnetic field[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(0):648-651. |
| [9] | 洪正军.铸轧法在铜盘管加工工艺中的应用[J].湖南冶金,2004(05):39-41. |
| [10] | 韩淑敏,刘刚,赵军.铸轧法生产H65黄铜带工艺研究[C].2006中国铜加工技术创新大会论文集,2006:281-291. |
| [11] | 钟卫佳;马可定;吴维治.铜加工技术使用手册[M].北京:冶金工业出版社,2007:1099-1100. |
| [12] | 卢德强.铸轧法和热轧法生产空调铝箔的工艺和产品对比[J].轻合金加工技术,2003(07):17-21. |
| [13] | 付亚波.铜合金冷凝管生产工艺探讨[J].有色金属加工,2007(06):39-40,51. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%