研究了不同配比的PC/PS共混体系的物理和力学性能及其与相容性的关系,结果表明,PS含量越高,拉伸强度、冲击强度、密度和吸水率等越低,而表面硬度和耐溶剂开裂能力则提高.通过DSC谱、SEM等实验结果表明,少量的辐射接枝共聚物PC-g-PS加入PC/PS共混体系,即能明显改善其相容性.加了共聚物以作为增容剂后,共混物的拉伸强度、冲击强度、密度、表面硬度和耐溶剂开裂能力均要比其相应的简单共混物的值来得高,而吸水率则有所下降.
参考文献
| [1] | Saeki S;Cowie J M G;Mcewen I J .[J].Polymer,1983,24(01):60. |
| [2] | Ouhadi T;Fayt R;Jerome R et al.[J].Journal of Applied Polymer Science,1986,32(06):5647. |
| [3] | Fayt R;Teyssie Ph .[J].Macromolecules,1986,19(07):2077. |
| [4] | Chen C C;Fontan E;Min K et al.[J].Polymer Engineering and Science,1988,28(02):69. |
| [5] | Kunori T;Geil P H .[J].Journal of Macromolecular Sciences:Physics,1980,18(01):93,135. |
| [6] | Eastmond G C .[J].Haraguchi Polymer,1983,24(09):1171. |
| [7] | Rudin A;Brathwaite N E .[J].Polymer Engineering and Science,1984,24(17):1312. |
| [8] | Mckay I D .[J].Journal of Applied Polymer Science,1991,42:281. |
| [9] | Jiang M;Huang X;Yu T .[J].Polymer,1985,26:1689. |
| [10] | 浦鸿汀,唐小真,罗荫培,徐祥铭.PC辐射接枝PS及其对PC/PS共混物的增容作用[J].高分子材料科学与工程,1998(03):75-78,83. |
| [11] | 李萍 .一种具有高分辨率的模拟信号采集及处理系统的研究[D].上海交通大学,1990. |
| [12] | CaiQ;Zhu S;Jiang L 等.[J].高分子材料科学与工程,1990,6(03):717. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%