本研究以陶瓷抛光废料为主要原料,辅以长石、球土、石英等,通过大量的探索性实验,确定了制备轻质建筑材料的基础配方.在此基础上,通过正交实验优化原料配方和工艺参数制备了高强轻质建筑材料.在球磨时间42rmin、烧成温度1170℃、保温时间15 min、添加剂含量5.5wt％时,制备出体积密度0.81 g/cm3、抗压强度14.25MPa、吸水率9.30％、导热系数0.30 W/m ·K的高强轻质建筑材料.
参考文献
| [1] | Anze Shui;Xiuan Xi;Yanmin Wang .Effect of silicon carbide additive on microstructure and properties of porcelain ceramics[J].CERAMICS INTERNATIONAL,2011(5):1557-1562. |
| [2] | E. Sanchez;J. Garcia-Ten;V. Sanz .Porcelain tile: Almost 30 years of steady scientific-technological evolution[J].CERAMICS INTERNATIONAL,2010(3):831-845. |
| [3] | Rambaldi E;Esposito L;Tucci A et al.Recycling of polishing poreelain stoneware residues in ceramic tiles[J].Journal of the European Ceramic Society,2007,27:3509-3515. |
| [4] | Sanchez E;Ibanez M J;Garcia-Ten J et al.Porcelain tile mierostructure:Implications for polished tile properties[J].Journal of the European Ceramic Society,2006,26:2533-2540. |
| [5] | 李丽匣,王亚琴,韩跃新,包士雷.陶瓷废料生产建筑材料的试验研究[J].东北大学学报（自然科学版）,2011(03):419-422. |
| [6] | 乔木,王欣丹,王艳,李丹.抛光砖抛光废料的回收利用途径分析[J].中国陶瓷,2011(01):25-28. |
| [7] | 税安泽,夏海斌,曾令可,程小苏,王慧,刘平安,金雪莉,吴细桂,简润桐.利用抛光砖废料制备多孔保温建筑材料[J].硅酸盐通报,2008(01):191-195. |
| [8] | 夏海斌,税安泽,陈培鑫,顾超然,杨静静,曾令可,程小苏,王慧,刘平安.环保型多孔陶瓷材料的影响因素研究[J].材料研究与应用,2008(04):284-286. |
| [9] | 俞康泰.陶瓷废料的再循环和环境材料学[J].佛山陶瓷,2003(09):36-37. |
| [10] | 董峰,郝洪顺,崔文亮,付鹏.陶瓷工业固体废弃物的回收再利用[J].硅酸盐通报,2006(03):124-127. |
| [11] | 徐建国.佛山陶瓷企业开展清洁生产的现状及方向[J].佛山陶瓷,2007(03):11-15. |
| [12] | 张全兆 .工程绝热材料导热系数与孔隙率、含水率关系的分析[J].河南机电高等专科学校学报,2000,8(02):47-49. |
| [13] | 衣乌.影响绝热材料导热系数的主要因素[J].保温材料与节能技术,2003(03):14-18. |
| [14] | 刘康时.陶瓷工艺学[M].广州:华南理工大学出版社,2003:99-104. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%