以Bi(NO3)3·5H2O,Fe(NO3)3·9H2O和柠檬酸为主要原料,采用液相自组装法,以OTS单分子层为模板,在ITO玻璃基片上成功制备了BiFeO3晶态薄膜.研究了退火温度以及保温时间对BiFeO3薄膜的影响.利用DSC/TG对铁酸铋前驱物结晶行为进行了表征,利用XRD和FE-SEM等测试手段对不同退火工艺下制备的BiFeO3薄膜进行了物相和表面形貌的表征.结果表明,BiFeO3晶态薄膜的结晶转变温度在440℃左右;实际上在550℃退火2h的条件下得到了纯相BiFeO3薄膜,薄膜表面致密,晶粒发育完整,尺寸均匀,无明显缺陷;退火温度过高,会导致杂相生成,晶粒异常长大;保温时间过长,会导致BiFeO3高温分解.
参考文献
| [1] | Liu H R;Liu T K;Wang X Z .[J].Solid State Communications,2009,149:1958-1961. |
| [2] | Tennon C;Yhery J;Baron T et al.[J].THIN SOLID FILMS,2006,515:481-484. |
| [3] | Kartavtseva M S;Gorbenko O;Yul Kaul A R et al.[J].THIN SOLID FILMS,2007,515:6416-6421. |
| [4] | Zhang G J;Cheng J R;Chen R et al.[J].Transactions of Nonferrous Metals Society of China,2006,16:s123-s125. |
| [5] | Liu H;Liu Z L;Liu Q et al.[J].THIN SOLID FILMS,2006,500:105-109. |
| [6] | Gao YF.;Masuda Y.;Koumoto K. .Microstructure-controlled deposition of SrTiO3 thin film on self-assembled monolayers in an aqueous solution of (NH4)(2)TiF6-Sr(NO3)(2)-H3BO3[J].Chemistry of Materials,2003(12):2399-2410. |
| [7] | Tan G Q;Song Y Y;Miao H Y .[J].Science China(Technological Sciences),2010,53(02):375-378. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%