采用电弧离子镀(AIP)技术在Ti6Al4V基体表面沉积制备了NiCrAlY涂层. 通过金相观察(OM)、扫描电镜(SEM)与能谱(EDS)分析、 X射线衍射(XRD)分析以及显微硬度测试, 研究了真空热处理对NiCrAlY涂层组织性能的影响, 讨论了Ti6Al4V基体/NiCrAlY涂层界面元素扩散规律. 结果表明: 700.℃真空热处理后, NiCrAlY涂层中开始析出γ′-Ni3Al相, 这提高了涂层的表面硬度; 在700.℃温度下, Ti6Al4V基体/NiCrAlY涂层界面由外至内出现Ni3(Al,Ti)、 TiNi和Ti2Ni中间化合物层, 并随着温度提高, 界面处中间化合物层增厚; 700.℃时, 主要发生了镍、钛元素的扩散, 铬元素在870.℃开始发生扩散. 当温度提高到950.℃后, 由于镍元素大量向Ti6Al4V基体扩散引起涂层的退化失效.
参考文献
| [1] | Zhou YC.;Tonomori T.;Yoshida A.;Liu L.;Bignall G.;Hashida T. .Fracture characteristics of thermal barrier coatings after tensile and bending tests[J].Surface & Coatings Technology,2002(2/3):118-127. |
| [2] | Leontiev S A;Kuznetsov V G;Rybnikov A I et al.Structure and properties of protective coating produced by vacuum arc deposition[J].Surface and Coatings Technology,1995,76-77(1-3):41-46. |
| [3] | Rybnikov A I;Tchizhik A A;Ogurtsov A P et al.The structure and properties of metal and metal-ceramic coatings produced by physical vapour deposition[J].Journal of Materials Processing Technology,1995,55(3-4):234-241. |
| [4] | 向兴华,陈康年,刘正义,李尚周,尹钟大,朱景川,全成军.等离子喷涂ZrO2-NiCoCrAlY梯度涂层的成分分布与力学性能[J].复合材料学报,2000(01):89-92. |
| [5] | Brindley W J;Miller R A .Thermal barrier coating life and isothermal oxidation of low-pressure plasma-sprayed bond coat alloys[J].Surface and Coatings Technology,1990,43:1-3: 446-457. |
| [6] | 郝杉杉,刘海平,汪晓红,冯自修,郝孟一,李金桂.真空电弧镀沉积NiCrAlY涂层工艺[J].材料工程,1999(02):40-42. |
| [7] | Li MH.;Zhang ZY.;Sun XR.;Li JG.;Yin E.;Hu WY.;Guan HR.;Hu ZQ. .Oxidation behavior of sputter-deposited NiCrAlY coating[J].Surface & Coatings Technology,2003(3):241-247. |
| [8] | 徐爱群;黄海波;王世栋 .磁控溅射NiCrAlY镀层的组织结构研究[J].东南大学学报(自然科学版),1996,26(04):136-138. |
| [9] | 曾潮流.溅射NiCrAlY涂层对Ti3Al金属间化合物氧化性能的影响[J].航空材料学报,1994(04):21. |
| [10] | Tang ZL.;Wu WT.;Wang FH. .Effect of MCrAlY overlay coatings on oxidation resistance of TiAl intermetallics[J].Surface & Coatings Technology,1998(3):248-252. |
| [11] | 唐兆麟;王福会;屮又 .MCrAlY涂层对TiAl金属间化合物抗高温氧化性能的影响[J].中国腐蚀与防护学报,1997,17(02):116-120. |
| [12] | Haiping Liu;Shanshan Hao;Xiaohong Wang;Zixiu Feng .Interaction of a near-α type titanium alloy with NiCrAlY protective coating at high temperatures[J].Scripta materialia,1998(10):1443-1450. |
| [13] | 刘桂兰;邹宇超 .回火温度对Ni-Cr-Al硬弹性合金组织和性能的影响[J].东北大学学报(自然科学版),1994,15(04):399-402. |
| [14] | 党刚.国外高温材料[M].上海:上海科学技术出版社,1963:35-80. |
| [15] | 王冰,黄荣芳,宫骏,王启民,梁越,孙超,闻立时,韩雅芳.Ni-Cr-Al-Y涂层真空热处理过程中元素的行为[J].金属学报,2000(10):1094-1098. |
| [16] | 汪晓红.Ti3Al基体/NiCrAlY涂层体系界面固态反应行为研究[J].航空材料学报,1997(04):8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%