利用拉伸实验和显微硬度测试等方法研究了不同阴极保护电位对Q235钢在3.5％NaC1溶液中氢脆敏感性的影响,并用SEM对断口形貌进行分析.结果表明,随着阴极保护电位的负移,Q235钢的最大抗拉强度和屈服强度没有呈现规律性变化,但断面收缩率减小,材料发生氢脆的可能性加大.当施加电位为-1100 mV时,断口出现准解理断裂特征形貌.
参考文献
| [1] | 孟超,曲政,庞其伟.1Cr18Ni9Ti海水循环水泵阴极保护参数[J].腐蚀与防护,2004(11):473-474,488. |
| [2] | S. Akonko;D. Y. Li;M. Ziomek-Moroz .Effects of cathodic protection on corrosive wear of 304 stainless steel[J].Tribology letters,2005(3):405-410. |
| [3] | S. Eliassen .New concept for cathodic protection of offshore pipelines to reduce hydrogen induced stress cracking (HISC) in high strength 13%Cr stainless steels[J].British Corrosion Journal,2004(1):31-37. |
| [4] | 杨兆艳,闫永贵,马力,张桂玲.阴极极化对907钢氢脆敏感性的影响[J].腐蚀与防护,2009(10):701-703. |
| [5] | 张国虎,龚敏,唐强,张婷,曾祥梅.用电化学方法研究X80管线钢的阴极保护参数[J].腐蚀与防护,2011(11):868-871,883. |
| [6] | 常娥,闫永贵,李庆芬,马力.阴极极化对921A钢海水中氢脆敏感性的影响[J].中国腐蚀与防护学报,2010(01):83-88. |
| [7] | Seok-Ki JANG,Min-Su HAN,Seong-Jong KIM.Electrochemical characteristics of stainless steel using impressed current cathodic protection in seawater[J].中国有色金属学报（英文版）,2009(04):930-934. |
| [8] | 李谋成,林海潮,曹楚南.碳钢在土壤中腐蚀的电化学阻抗谱特征[J].中国腐蚀与防护学报,2000(02):111-117. |
| [9] | 徐海波,王廷勇,王远志,朱勇,彭荣,兰翔.16Mn钢在土壤中的阴极保护参数实验室评价技术研究[J].腐蚀科学与防护技术,2006(06):404-409. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%