用注射压铸方法制造了直径为1.0 mm的棒状Nd8 Fe87.5B4.5纳米复合永磁体,分别用电脉冲和传统等温退火方法对样品进行了均匀热处理,并用X射线衍射(XRD)和透射电镜(TEM)分析了样品的微结构.结果发现,经电脉冲方法退火的样品晶粒尺寸比用传统等温炉退火更规则更均匀,使Hc和(BH)m分别提高16.5%和13.4%.
参考文献
[1] | Kneller E.F.;Hawig R. .The exchange-spring magnet: a new material principle for permanent magnets[J].IEEE Transactions on Magnetics,1991(4):3588-3560. |
[2] | Skomski R;Coey J M D .[J].Physical Review,1993,B 48:15812. |
[3] | Manaf A;Buckley R A;Davies H A .[J].Journal of Magnetism and Magnetic Materials,1993,128:302. |
[4] | Gutfleisch O;Gebel B;Mattern N .[J].Journal of Magnetism and Magnetic Materials,2000,210:5. |
[5] | Kramer MJ.;Lewis LH.;Fabietti LM.;Tang Y.;Miller W.;Dennis KW. McCallum RW. .Solidification, microstructural refinement and magnetism in Nd2Fe14B [Review][J].Journal of Magnetism and Magnetic Materials,2002(1):144-155. |
[6] | Zhang W.;Inoue A. .Bulk nanocomposite permanent magnets produced by crystallization of Fe66.5Co10Pr3.5B20 bulk glassy alloy[J].Journal of Applied Physics,2002(10 Pt.3):8834-8836. |
[7] | Marinescu M et al.[J].Journal of Magnetism and Magnetic Materials,2005,290-291:1267. |
[8] | Wang Ying;Wang Erde .[J].Journal of Magnetism and Magnetic Materials,2007,312:220. |
[9] | 韩广兵,高汝伟,陈伟,李卫,李岫梅,冯维存.晶化热处理条件对Nd2(FeCo)14B/α-Fe纳米复合材料磁性能的影响[J].功能材料,2003(05):511-512. |
[10] | Li X H;Gao Z S et al.[J].Materials Letters,2005,59:2782. |
[11] | Cullity B D.Element of X-ray Diffraction[M].Ma:addison-wesley,1978:100. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%