The precipitation of Ti(V)N(C)in high-carbon steel PD_3 during thermomechanicol treatment at austenitic temperatures after deformation has been observed.The average size of Ti(V)N(C)particles may reduce with the increase of strain and the decrease of thermomechanical treatment temperature,and vise versa.The growth of Ti(V)N(C)particles at 920°C is found to be controlled by the interface reaction between precipitated particles and matrix.