采用动态激光光散射(DLS)研究了单体、引发剂和乳化剂用量对微乳液聚合PMMA的粒径及分布、分子量的影响.DLS分析结果表明,PMMA的粒径为25～60nm,M-w 为1×106～5×106.随单体用量增大,PMMA粒径变大;随引发剂用量增大,PMMA粒径变小;PMMA粒径分布随单体和引发剂用量提高而变宽.在8%～12%(质量分数)范围内,随乳化剂用量增大PMMA粒径增大,分布变窄,然后随着乳化剂用量的进一步增加,PMMA粒径减小.引发剂用量减少和乳化剂用量增加均使PMMA分子量提高.FT-IR和DSC分析结果表明,采用微乳液聚合方法制备的PMMA是以间规立构为主,PMMA分子链的局部有序性得到了提高.
参考文献
| [1] | Atik S S;Thomas J K .[J].Journal of the American Chemical Society,1981,103:4279. |
| [2] | Atik S S;Thomas J K .[J].Journal of the American Chemical Society,1982,104:5868. |
| [3] | Ferrick M R;Murtagh J;Thomas J K .[J].Macromolecules,1989,22:1515. |
| [4] | GuoJS;Sudol E D;Vanderhoff J W et al.[J].Journal of Polymer Science Part A:Polymer Chemistry,1992,30:691. |
| [5] | GuoJS;Sudol E D;Vanderhoff J W et al.703[J].Journal of Polymer Science Part A:Polymer Chemistry,1992,30:703. |
| [6] | Gan L M;Chew C H;Lee K C et al.[J].Polymer,1994,35:2659. |
| [7] | Rodrigue L A;Mendizabal E;Puig J E .[J].Journal of Applied Polymer Science,1993,48:775. |
| [8] | Bleger F;Murthy A K;Pla F et al.[J].Macromolecules,1994,27:2559. |
| [9] | 徐相凌;葛学武;张志成.[J].高分子学报,1998(06):658. |
| [10] | 徐相凌,葛学武,张志成,张曼维,左榘,牛爱珍.偶氮二异丁腈引发甲基丙烯酸甲酯微乳液聚合[J].中国科学技术大学学报,2000(01):62-68. |
| [11] | 廖勇勤,王琪,王良文.超声辐照引发MMA微乳液聚合产物结构表征[J].高分子材料科学与工程,2000(06):144-146,150. |
| [12] | 薛奇.高分子结构研究中的光谱方法[M].北京:高等教育出版社,1995 |
| [13] | Yan F.;Zhai XD.;Zhao DJ.;Zheng CR. .Preparation and characterization of polyacrylamide in cationic microemulsion[J].Journal of Applied Polymer Science,1998(4):747-754. |
| [14] | 严锋,郑昌仁,韦亚兵.阳离子型微乳液聚合丙烯酰胺的表征[J].高等学校化学学报,2000(04):655-656. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%