基于凝固收缩的板坯铸机辊缝研究

钢铁, 2008, 43(3): 44-48.

1.首钢集团总公司技术研究院,北京,100043

2.首钢集团总公司技术研究院,北京,100043

3.首钢集团总公司技术研究院,北京,100043

4.首钢集团第二炼钢厂,北京,100043

Study on Roll Gap of Slab Caster Based on Solidification Shrinkage

为了研究辊缝收缩对减轻板坯中心偏析的作用,采用数值模拟方法计算了板坯的温度场和凝固收缩,分析了坯壳厚度和凝固收缩量在冶金长度内的分布,建立了3种辊缝收缩实验方案并比较了其效果.结果表明,在凝固末端以前2～3个扇形段进行辊缝收缩有效减轻了板坯中心偏析,辊缝收缩量应略大于铸坯自由凝固收缩量.

[1]	Ma C W;Shen H F;Huang T Y et al.Numerical Simulation on Macro-Segregation in Steel Ingot During Solidification[J].ACTA METALLURGICA SINICA,2004,17(03):288.
[2]	Lamant J Y;Larrecq M;Smarzynski z et al.Investigation of slab Bulging During Continuous Casting by Simulation on a Plasticine Model[J].Transactions ISU,1984,24(05):B81.
[3]	Hattori M;Nagata S;Inaba A et al.Development of Technology to Eliminate Centerline Segregation in Continuously Cast Slabs[J].Ironmaking and Steelmaking,1989,16(06):34.
[4]	汪洪峰,汪峰,沈国强.板坯连铸机辊缝控制技术的应用[J].炼钢,2004(05):27-29.
[5]	王三忠,高新军,王保卫,王中歧,史学玉.板坯三角区裂纹的产生与防止[J].连铸,2003(01):42-43.
[6]	《铸造工程师手册》编写组.铸造工程师手册[M].北京:机械工业出版社,1997
[7]	杨志军,王海舟.用原位分析方法研究连铸板坯的偏析和夹杂[J].钢铁,2003(03):61-63.

上一张下一张

计量

作者相关

文章评分