综述了海洋防腐涂料的体系组成、腐蚀机制和研究发展趋势;介绍了环氧富锌底漆和热喷锌铝底层、环氧玻璃鳞片中涂漆和高耐候性面漆的腐蚀特点的研究现状.和海洋涂料的评价与检测方法；指出了海洋防腐涂料的发展趋势.
This paper summarized the types,corrosion characteristics and research trend of paints for marine application.Firstly,the current research status of zinc-rich epoxy primer,and thermal sprayed aluminum and zinc layer,glass-flaked epoxy paint,and super anti-aging top-coat were introduced.Secondly,the appraisal and test methods of paints for marine application were introduced.Finally,the trend of the research and development of paints for marine application were indicated.
参考文献
| [1] | Geeta P,Deepak S,Pramod K.Ethyl silicate binders for high performance coatings［J］,Progress in Organic Coatings,2001,42:1.[2] Marchebois H,Touzain S,Joiret S,et al. Zinc-rich powder coatings corrosion in sea water: influence of conductive pigments[J]. Progress in Organic Coatings, 45:415 [3] Pereira D,Scantlebury J D,Ferreira M G S,et al. The application of electrochemical measurements to the study and behaviour of ainc-rich coatings[J]. Corrosion Science, 30:1135[4] Vilche J R,Bucharsky E C,Giudice C A. Application of EIS and SEM to evaluate the influence of pigment shape and content in ZRP formulations on the corrosion prevention of naval steel[J]. Corrosion Science, 44:1287[5]Marchebois H,Savall C,Bernard J,et al,Electrochemical behavior of zinc-rich powder in artificial sea water［J］.Electrochimica Acta,2004,49:2945.[6] Marchebois H,Joiret S,Savall C,et al. Characterization of zinc-rich powder coatings by EIS and rman spectroscopy[J]. Surface and Coatings Technology, 157:151[7] Battocchi D,Simoes A. M,Tallman D E,et alElectrochemical behaviour of a Mg-rich primer in the protection of Al alloys[J]. Corrosion Science, 48:1292[8]李守本,王瑞雪,姚平.锌铝合金丝及其热喷涂涂层的电化学特性［J］.材料开发与应用,1998,6：18.[9]Gartland P O.Cathotic protection of aluminum-coated steel in seawater［J］.Materials Performance,1987,26(6):29.[10]Fisher K P,Thomason W H,Finnegan J E.Electrochemical performance of flamed-sprayed aluminum coatings on steel in seawater［J］.Materials Performance,1987,26(9):35.[11]Thomason W H.Cathodic protection of submerged steel with thermal srayed aluminum coatings［J］.Material performance,1985,24(3):20.[12]赖国伟,谢晓君,武自修,等.金属喷涂长效复合防护涂层在海洋大气环境中的应用［J］.材料开发与应用,2002,17：29.[13]李言涛，侯保荣，海洋环境下热喷涂锌、铝及其合金涂层防腐蚀机理研究概况［J］.材料保护,2005,38（9）：30.[14] 王爱华,李伟华,侯保荣. 浅谈海工混凝土结构防腐涂料[J]. 山西建筑, 33(21):19 [15] Sathiyanarayanan S,Syed Azim S,Venkatachari G. Corrosion protection coating containing polyaniline glass flake composite for steel[J]. Electrochimica Acta, 53:2087[16]刘福春,郝永胜,王震宇,等.聚苯胺改性玻璃鳞片环氧重防腐涂料及其制备方法［P］.申请号：200810012655.5,2008-08-06.[17]刘福春,郝永胜,王震宇,等.聚苯胺改性玻璃鳞片聚酯重防腐涂料及其制备方法［P］.申请号：200810012659.3,2008-08-06.[18]刘福春,郝永胜,王震宇,等.聚苯胺改性玻璃鳞片乙烯基酯重防腐涂料及其制备方法［P］.申请号：200810012658.9,2008-08-06.[19] 向斌 ,吴丹刚,刘建武,100％固体份刚性聚氨酯重防腐涂料及其在海洋工程中的应用[J]. 水运工程,2005,377:29[21]Shi H W,Liu F C,Yang L H,Han E H,et al.Characterization of protective performance of epoxy reinforced with nanometersized TiO2 and SiO2[J]. Progress in Organic Coatings, 62:359[20]刘福春,杨立红,陈群志,等.纳米复合氟碳涂料的性能研究［J］.腐蚀科学与防护技术,2004,16:343.[21]刘福春,韩恩厚,柯伟.抗紫外纳米TiO2/ZnO复合丙烯酸酯涂料［J］.材料研究学报,2003,17:138.[22]刘福春,韩恩厚,柯伟.一种纳米抗紫外丙烯酸酯涂料［P］.中国专利：ZL01128270.3,2004-12-15.[23] Yang L H,Liu F C,Han E H. Effects of P/B on the properties of anticorrosive coatings with different particle size[J]. Progress in Organic Coatings, 53:91[24]刘福春,韩恩厚,柯伟.一种纳米抗紫外聚氨酯涂料［P］.中国专利：ZL01128269.X,2005-01-26.[25] 邵怀启,韩文礼,王雪莹,等. 海洋平台防腐蚀涂料技术进展[J]. 中国海洋平台, 22(5):6[26]阎明久.海洋重防腐涂料的发展与成熟化思考［J］.涂料工业,2001,6:44.[27]刘志，杨小刚，王彝，田边弘往，侯保荣，超厚膜环氧重防腐涂料的耐中性盐雾性能研究［J］.涂料工业，2009,39(3):57.[28]Cavalcanti E,0.Ferraz,The use of electrochemical impedance measurements to assess the performance of organic coating systems on naval steel［J］.Progress in Organic Coatings,1993,23:186.[29] Le Thu Q,Takenouti H,Touzain S. EIS characterization of thick flawed organic coatings aged under cathodic protection in seawater[J]. Electrochimica Acta, 51:2491[30]Elaine A,Ramon O,Francisco L,et al.Marine paint fomulations:Conducting polymers as anticorrosive additives［J］,Progress in Organic Coatings,2007,59:46.[31]Collazo A,Novoa X R,Perez C,Corrosion behaviour of cermet coatings in artificial seawater［J］.Electrochimica Acta,1994,44:4289.[32] 黄月文,刘伟区. 含硅(甲基)丙烯酸酯在涂料工业中的研究和应用进展[J]. 涂料工业, 36(11):57 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%