利用静态挂片失重法研究了含H2S／CO2模拟油田水溶液中，温度及Cl^-浓度对L360管线钢点蚀的影响，并利用Gumbel第一类近似函数分析了最深蚀孔概率．结果表明，在40℃-70℃之间，Cl^-1浓度为10g／L条件下，点蚀的严重程度随温度增高而增大．恒定温度下，C1^-1浓度对点蚀发生也有明显的影响，当Cl在10-15g／L范围时，腐蚀试样发生明显的点蚀；当Cl^-浓度大于20g／L时，试样主要发生均匀腐蚀，随着Cl^-浓度的增大，腐蚀产物膜变得更加疏松，保护性能下降，均匀腐蚀速率增大．最深点蚀分布服从Gumbel第一类近似函数．
The effect of temperature and Cl^- concentration on pitting corrosion of L360 steel in H2S/CO2 environment has been studied using methods of mass loss testing, SEM and XRD. The depth distribution of pits was analyzed with Gumbel first approximating function. The results showed that pitting corrosion tended to be more serious with the increase of temperature （from 40 ℃ to 70 ℃） in 10 g/L Cl^- solution. Pitting corrosion occurred in Cl^- solution with the concentration of 10-15 g/L at constant temperature, and uniform corrosion ccurred when the Cl^- concentration was higher than 20 g/L. As the temperature increased, corrosion products on the surface became looser and the protective property decreased. The measured maximum depth of pits followed the Gumbel first approximating function.
参考文献
| [1] | 崔之健,史秀敏,李又绿.油气储运设施腐蚀与防护[M].北京:石油工业出版社,2009. |
| [2] | 李鹤林,白真权,刘道新等.模拟油田H2S/CO2环境中N80钢的腐蚀及影响因素研究[J].材料保护,2003,36(4):32. |
| [3] | Fierro G, Ingo G M, Mancia F. XPS investigation on the corrosion behavior of 13Cr martensitic stainless steel in CO2-H2S-C1 environments[J]. Corrosion, 1989, 45(10): 814. |
| [4] | Fierro G, Ingo G M, Mancia F. XPS Investigation on AISI 420 stainless steel corrosion in oil and gas well environments [J]. Mater. Sci., 1990, 25 (2): 1407. |
| [5] | 周计明.油管钢在含CO2/H2S高温高压水介质中的腐蚀行为及防护技术的作用[D].西安:西北工业大学,2002. |
| [6] | Ren C Q, Liu D X, Bai Z Q, et al. Corrosion behavior of oil tube steel in simulant solution with hydrogen sulfide and carbon dioxide[J]. Mater. Chem. Phys., 2005, 93(2-3): 305. |
| [7] | Hamdy A S, Sa'eh A G, Shoeib M A, et al. Evaluation of corrosion and erosion-corrosion resistances of mild steel in sulfide-containing NaCl aerated solutions[J]. Electrochim. Acta, 2007, 52(24): 7068. |
| [8] | 曹楚南.腐蚀试验数据的统计分析[M].北京:化学工业出版社,1988:91. |
| [9] | 王水勇,任爱.利用Gumbel极值分布预测管道最大腐蚀深度[J].腐蚀科学与防护技术,2008,20(5):358. |
| [10] | Schmitt G. Fundamental aspects of CO2 corrosion[A]. Hausler R, Giddard H P. Corrosion[C]. Houston: NACE International, 1984, No. 84010. |
| [11] | Yin Z F, Zhao W Z, Bai Z Q, et al. Corrosion behavior of SM 80SS tube steel in stimulant solution containing H2S and CO2[J]. Electrochim. Acta, 2008, 53(10): 3690. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%