对结晶器电磁搅拌(M-EMS)在邯钢8机8流方坯连铸机使用情况和效果进行了分析和研究，M-EMS能够提高连铸方坯表面质量和内部质量，改善连铸坯中心疏松、缩孔和中心偏析以及减少角裂漏钢；同时对方坯应用M-EMS过程中存在的钢水过热度过高、电磁搅拌线圈漏水和浸入式水口渣线恶化等问题，提出了相应的改进措施。
The effect of mold electromagnetic stirring ( M-EMS ) on Hangang eight machine eight strand billet caster are analyzed and studied, M-EMS can enhance the continuous casting billet surface quality and internal quality, improve the continuous casting slab center porosity, shrinkage and center segregation and reduce corner cracking breakout of billet; at the same time, in the process of M-EMS application, such problems will occur, molten steel superheat is exorbitant, electromagnetic stirring coil water leakage and worse immersed nozzle slag line, and corresponding improvement measures were put forward.
参考文献
| [1] | |
| [2] | .参考文献[2] 于艳等.结晶器电磁搅拌对连铸坯质量的影响.钢铁,2005,(2)[3] 蔡开科.浇铸与凝固[M].北京:冶金工业出版社,1987[4]张宏丽,贾交霖,王恩刚,等.电磁搅拌改善铸坯内部质量的实验研究[J].东北大学学报(自然科学版,2001,22(3):315-318[5]杨吉春,蔡开科,郭殿锋,等.结晶器电磁搅拌对重轨钢大方坯中心碳偏析的影响[J].特殊钢,2003,24(3):6-8[6]林守连等.电磁搅拌对连铸方坯质量的影响).[J].连铸,2003,(2):- |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%