研究了RE-Mg-Ti复合变质对高碳高速钢组织和性能的影响.结果表明,复合变质能细化高速钢基体,并且使共晶碳化物由层片状变成球状.变质处理后,高碳高速钢的硬度、红硬性和强度变化不大,断裂韧性和疲劳裂纹扩展门槛值有所提高,冲击韧性提高一倍以上,抗热疲劳性能和高温耐磨性也明显改善.
参考文献
[1] | 桥本光生;大有清司;吉田幸一郎.CPCプロセスにょる强韧ロ-ルの开发[J].制铁研究(日本),1990(338):62-66. |
[2] | George J. McManus .Speedy advance predicted for high speed steel rolls[J].Iron & Steel Review,1999(3):59-60. |
[3] | 宋延沛,李秉哲,朱景芝,谢敬佩,周国峰.稀土复合变质剂对高碳高速钢性能及组织的影响[J].钢铁研究学报,2001(06):31-34. |
[4] | Gierek A.The Effect of Modifiers on the Structure of S6-5-2High-Speed Steel[J].Zesz Nauk Politech Slask,1982(23):5-20. |
[5] | Frost R H;Majewski T;Krauss G .Impact Fracture Behavior ofHigh Chromium-Molybdenum White Cast Irons[J].AFS Transactions,1986,94:297-322. |
[6] | 邓玉昆;陈景榕;王世章.高速工具钢[M].北京:冶金工业出版社,2002 |
[7] | 马臣.Effect of Rare Earth Elements on Thermal Fatigue of High Ni-Cr Alloy Cast Iron[J].JOURNAL OF RARE EARTHS,1996(04):286. |
[8] | 刘佐民 .M50高速钢高温摩擦磨损特性的研究[J].摩擦学学报,1997,17(01):38-44. |
[9] | Zum-Gahr K H .How Microstructure Affects Abrasive Wear Re-sistance[J].Metal Progress,1979,116(04):46-52. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%