以现场高炉渣化学成分为基准,利用纯化学试剂制备试验渣样,研究了高铝中钛型高炉渣脱硫的动力学过程,确定了其脱硫的动力学参数。结果表明,当反应温度一定时,铁水中硫含量w（[S]）随脱硫反应时间的延长而降低。试验条件下,高铝中钛渣脱硫过程属于二级反应,其限制性环节是硫在熔渣中的扩散。熔渣中硫的传质系数βS随着温度的升高而增大,硫在熔渣中的扩散活化能ED为127.03kJ/mol。
On the basis of the compositions of blast furnace（BF） slag at field,the desulphurization dynamics process was researched for BF slag with medium titanium and high alumina content,which was fabricated from pure chemical agents.The dynamics parameters of desulphurization were obtained.Results show that the sulfur content in liquid iron（w（[S]）） decreases with the elongation of desulphurization reaction time when the temperature is constant.Under the experimental conditions,the desulphurization process of BF slag with medium titanium and high alumina content belongs to second-order reaction,the restricted step of which is sulfur diffusion in the fused slag.The mass transfer coefficient（βS） rises with increasing the reaction,and the diffusion activation energy（ED） of sulfur element in fused slag is 127.03 kJ/mol.
参考文献
| [1] | 张振峰 .承钢高炉钒钛炉渣性能研究[D].沈阳:东北大学,2009. |
| [2] | 文玲,张金柱.含钛高炉渣性能的研究进展[J].钢铁研究学报,2011(05):1-3,19. |
| [3] | 张振峰,吕庆,李福民.高Al2O3钒钛炉渣熔化性能的实验研究[J].东北大学学报(自然科学版),2007(10):1414-1416,1420. |
| [4] | 姚廷利,马锡民.承钢1260m3高炉钒钛矿强化冶炼实践[J].炼铁,2008(02):37-40. |
| [5] | 王喜庆.论高钛型炉渣高炉冶炼中TiO2的属性[J].钢铁钒钛,1989(02):1. |
| [6] | 曲彦平;邵桂春 .MnO高钛渣脱硫动力学的研究[J].沈阳工业大学学报,1998,20(02):24. |
| [7] | 鄢毓璋;兰洪 .高炉低钛渣脱硫动力学的研究[J].金属学报,1991,27(04):224. |
| [8] | 白晨光 .含钛高炉渣的若干物理化学问题研究[D].重庆大学,2003. |
| [9] | 郭兴忠;文光远;张丙怀.中钛型高炉渣冶金性能的研究[J].四川冶金,2000(03):18. |
| [10] | 汪任凭,罗果萍,张小伟.包钢特殊渣脱硫动力学研究[J].包头钢铁学院学报,2006(03):214-217. |
| [11] | 王庆祥,何环宇.渣-铁反应脱硫动力学研究[J].包头钢铁学院学报,2001(03):207-209. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%