Stirring assisted brazing of SiC(p/A356) composites in air was investigated. A stirring was applied on one of the samples to be bonded at 455℃ during brazing. The filler metal was extruded and impacted intensively on the two surfaces of the base materials during stirring. It can be found that oxide film on the surface of the composites can be disrupted and removed through the observation by scanning electron microscopy (SEM). The metallurgical bonds formed between the filler metal and the base materials. However, continuous residual oxide film was found at bottom joint interface, which limited the lift of joint strength. A stirring was applied once more after the samples were continuously heated up to 470 and 500℃, respectively. At this time, residual oxide film after the first of stirring can be broken by once more stirring. The bonds are mainly composed of a new alloy, which have a higher content of aluminum and are free of continuous oxide film, showing higher shear strength of 113 MPa than that of the base materials.
参考文献
| [1] | A. Urena;M. D. Escalera;L. Gil .Influence of interface reactions on fracture mechanisms in TIG arc-welded aluminium matrix composites[J].Composites science and technology,2000(4):613-622. |
| [2] | D.Q. Sun;X.Y. Gu;W.H. Liu .Transient liquid phase bonding of magnesium alloy (Mg-3Al-lZn) using aluminium interlayer[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):29-33. |
| [3] | H. W. Liu;C. Guo;Y. Cheng .Interfacial strength and structure of stainless steel-semi-solid aluminum alloy clad metal[J].Materials Letters,2006(2):180-184. |
| [4] | M. Kiuchi;J. Yanagimoto;S. Sugiyama .Application of mushy/semi-solid joining--Part 3[J].Journal of Materials Processing Technology,2003(1/3):163-166. |
| [5] | A.Narimannezhad;H.Aashuri;A.H. Kokabi;A.Khosravani;M.Kiani;A.Forough .Semisolid Joining of Zinc AG40A Ailoy by Partial Remelting and Mechanical Stirring[J].Diffusion and Defect Data. Solid State Data, Part B. Solid State Phenomena,2008(0):225-230. |
| [6] | A. Narimannezhad;H. Aashuri;A. H. Kokabi;A. Khosravani .Microstructural evolution and mechanical properties of semisolid stir welded zinc AG40A die cast alloy[J].Journal of Materials Processing Technology,2009(8):4112-4121. |
| [7] | H. B. Xu;Q. X. Xing;Y. L. Zeng .Semisolid stirring brazing of SiCp/A356 composites with Zn27Al filler metal in air[J].Science and Technology of Welding and Joining,2011(6):483-487. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%