采用熔融玻璃净化和循环过热相结合的方法,在Ni-Si共晶合金中取得了最大330K的大过冷度.研究了大块过冷Ni-Si共晶合金晶粒细化,发现在某一关键过冷度(△T*=184K)以上,合金晶粒尺寸明显细化.实验证实在过冷Ni-Si共晶合金中枝晶重熔和碎断是晶粒细化的主要原因.为了更好地分析其晶粒细化机制,基于枝晶生长LKT-BCT模型完成了相关的计算.

参考文献

[1] Qin F X;Zhang H F;Ding B Z et al.[J].Intermetallics,2004,12:1197.
[2] Jia J H;Lu J J;Zhou H D et al.[J].Materials Science and Engineering,2004,A381:80.
[3] Lu G J;Earl T et al.[J].Electrochimica Acta,2004,49:1461.
[4] 徐祖耀;李鹏兴.材料科学导论[M].上海:上海科学技术出版社,1986
[5] Waker J W;Pierre G R St.The physical chemistry of process metallurgy, part 2[M].Inter Science, New York,1959:845.
[6] Kattamis T Z;Flemings M C .[J].Journal of Crystal Growth,1976,34:215.
[7] Abbaschian G J;Flemings M C .[J].Metallurgical and Materials Transactions,1983,14A:1147.
[8] Eckler H;Schwarz M;Karma A et al.[J].Materials Science Forum,1996,45:215.
[9] Ecker H;Norman A F;Gartner F et al.[J].Journal of Crystal Growth,1997,82:3787.
[10] Horvay G .[J].International Journal of Heat and Mass Transfer,1965,8:1959.
[11] Glicksman M E .[J].Acta Materialia,1965,13:1231.
[12] Jackson K A;Hunt J D;Uhlmann D R .[J].Journal of Materials Science Letters,1969,245:407.
[13] Kattamis T Z;Flemings M C .[J].Transactions AIME,1966,236:1523.
[14] Ovsyenko D E;Masiov V V;Dneprenko V N.[J].Russian Metallurgy,1979(06):124.
[15] Mullis A M;Cohrane R F .[J].Journal of Applied Physics,1997,82:1380.
[16] Karma A.[J].International Journal of Non Equilibrium Processing,1998(11):201.
[17] NASH P;Nash A.Phase diagrams of binary nickel alloy[M].Materials Park. OH:ASM International,1991:229.
[18] Goetzinger R.;Herlach DM.;Barth M. .Growth of lamellar eutectic dendrites in undercooled melts[J].Journal of Applied Physics,1998(3):1643-1649.
[19] Lu Feng;Guo Xuefeng;Yang Gencang .[J].Journal of Crystal Growth,219:489.
[20] Lipon J;Kurz W;Trivedi R .[J].Acta Materialia,1987,35(04):957.
[21] Trivedi R;Lipton J;Kurz W .[J].Acta Materialia,1987,35(04):965.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%