为了简化已有阻垢缓蚀荆的制造工艺,降低生产成本,以水为溶剂,过硫酸盐为引发剂,用乙烯磺酸钠(SVS)、丙烯酸羟丙酯(HPA)和丙烯酸(AA)合成了兼具阻垢分散特性和缓蚀性能的AA-HPA-SVS共聚物,按国家标准对其阻垢和缓蚀性能进行了研究.结果表明:AA-HPA-SVS三元共聚物对中性介质中CaCO<,3>和Ca<,3>(PO<,4>)<,2>的阻垢效果良好,对Fe<,2>O<,3>的分散性能较好;AA-HPA-SVS共聚物对碳钢具有一定的缓蚀作用,与Na<,2>MoO<,4>复配后缓蚀性能显著提高,20 mg/L AA-HPA-SVS三元共聚物和150 mg/L Na<,2>MoO<,4>组成的复配缓蚀剂对CaCO<,3>的阻垢率可达95%,对碳钢缓蚀率达85%,同时不影响原三元共聚物对Fe2O<,3>的分散性能.AA-HPA-SVS三元共聚物应用面广,阻垢和缓蚀综合性能好.
参考文献
| [1] | 唐酞峰.循环冷却水阻垢缓蚀剂的研制[J].腐蚀科学与防护技术,2007(06):444-446. |
| [2] | R. Touir;M. Cenoui;M. El Bakri;M. Ebn Touhami .Sodium gluconate as corrosion and scale inhibitor of ordinary steel in simulated cooling water[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(6):1530-1537. |
| [3] | Choi DJ.;You SJ.;Kim JG. .Development of an environmentally safe corrosion, scale, and microorganism inhibitor for open recirculating cooling systems[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):228-235. |
| [4] | 荆国华,周作明,唐受印,戴友芝.MA-AMPS共聚物的制备及其性能研究[J].水处理技术,2002(02):82-85. |
| [5] | 田玲,王九思,李玉金.AA/AMPS 二元共聚物的合成及阻垢性能研究[J].兰州交通大学学报,2005(01):81-83. |
| [6] | 喻献国,李国希,杨军,伍协,胡金丰.马来酸酐三元共聚物的阻垢、分散及缓蚀性能[J].材料保护,2003(02):1-3. |
| [7] | 唐宏科,王磊.马来酐-丙烯酰胺-丙烯酸羟乙酯共聚阻垢剂的研究[J].工业水处理,2006(06):50-53. |
| [8] | 陆建民;胡洪;黄燕 .冷却水处理剂分散氧化铁沉积能力的评定[J].工业水处理,1991,11(06):10-12. |
| [9] | 郭英,宋诗哲.工业纯铁/盐酸体系中聚丙烯酸的缓蚀作用机理[J].化工学报,2000(06):788. |
| [10] | 刘红 .钼系复合配方的缓蚀性能研究[J].武汉科技大学学报（自然科学版）,1999,22(04):348-350. |
| [11] | 曹楚南;张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:167-168. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%