研究了时效工艺对FeMnSiCrNiNbC合金形状记忆效应、冷却到室温的回复应力以及Ms温度的影响,通过SEM分析了微观组织的变化.结果表明:在800℃时效时,与直接时效相比,10%室温形变后时效对合金的形状记忆效应、冷却到室温的回复应力以及Ms温度提高更加显著;形变后产生的晶体缺陷提供了NbC的形核位置,使NbC的析出速度和析出数量显著增加,粒径减小,因而对基体的强化效果更显著.同时NbC粒子产生的弹性应力场也有助于应力诱发ε马氏体转变的可逆性.
参考文献
| [1] | Kaneaki Tsuzaki;Masahiko Ikegami;Yo Tomota .[J].ISIJ International,1990,30(08):666. |
| [2] | Ohtsuka H;Kajiwara S;Ishihara T .[J].Materials Characterization,1994,32:229. |
| [3] | Wang Y Q;Wang Z;Yang J H .[J].Scripta Materialia,1997,36(07):741. |
| [4] | Wen Y H;Li N;Xiong L R .[J].Materials Science and Engineering,2005,A407:31. |
| [5] | Otsuka H;Murakami M;Matsuda S .[J].Shape Memory Materials,1988,9:451. |
| [6] | Baruj A;Kikuchi T;Kajiwara S .[J].Materials Science and Engineering,2004,A378:333. |
| [7] | Kajiwara S .[J].Scripta Materialia,2001,44(12):2809. |
| [8] | Dong Z Z;Kajiwara S;Kikuehi T et al.[J].Acta Materials,2005,53:4009. |
| [9] | 文玉华;李宁;胥永刚 .[P].CN 02133699.7,2003. |
| [10] | Wen Y H;Yan M;Li N .[J].Scripta Materialia,2004,50:835. |
| [11] | 李宁,文玉华,陈孟诗,涂铭旌,李平全,刘迎来,马颖丽.时效温度对Fe-Mn-Si-Cr-Ni-C记忆合金回复应力的影响[J].功能材料,2000(05):501-502. |
| [12] | 李宁,文玉华,刘建辉,涂铭旌.影响Fe-Mn-Si-Cr-Ni形状记忆合金相变点的因素[J].功能材料,2002(01):44-45,48. |
| [13] | 徐祖耀.形状记忆材料[M].上海:上海交通大学出版社,2002:200. |
| [14] | 潘金生;仝健民;田民波.材料科学基础[M].北京:清华大学出版社,1998:590. |
| [15] | Wen Y H;Li N;Xiong L R .[J].Materials Science and Engineering,2005,A407:31. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%