Research on Effect of Rare Earth Compounds in Phosphating Process

稀土学报(英文版), 2004, 22(z3): 262-265.

^1, , ^2, , ^3, , ^4, , ^5, , ^6, , ^7,

1.Deptment of Chemistry and Chemical Engineering , Foshan University, Foshan 528000, China

2.Deptment of Chemistry and Chemical Engineering , Foshan University, Foshan 528000, China

3.Deptment of Chemistry and Chemical Engineering , Foshan University, Foshan 528000, China

4.Deptment of Chemistry and Chemical Engineering , Foshan University, Foshan 528000, China

5.Deptment of Chemistry and Chemical Engineering , Foshan University, Foshan 528000, China

6.Deptment of Chemistry and Chemical Engineering , Foshan University, Foshan 528000, China

7.Deptment of Chemistry and Chemical Engineering , Foshan University, Foshan 528000, China

Research on Effect of Rare Earth Compounds in Phosphating Process

Keywords： phosphating

The effect of REC on appearance, weight and coating corrosion resistance was discussed, of which results suggest that addition of a small quantity of the REC into phosphating bath is very advantageous in terms of coating resistance to corrosion and depositing speed, and the scale of optimizing doses of REC added in bath is 30 ～ 55 mg ·L -1.Through analyses of configurations and components of films by SEM and EDS, it was ascertained that the samples gained in bath added REC, relative to the sample got in bath without REC, improve the coating inoxidizability because of increasing of covering rate of sheet crystals in the surface, and the sequence of what elements P, Fe and Zn contribute to erosion resistance of films is Fe ＞ P ＞ Zn.

参考文献

[1]	Kubicki J.In: Pracownia Techniki Przeciwkoro-Zyjnej[M].WSiP(in Polish),Warszawa,1977
[2]	Ang K F;Turgoose S .Development of phosphate coatings on mild steel[J].Transactions of the Institute of Metal Finishing,1991,69(02):58.
[3]	Ghali E L;Potvin R J A .The mechanism of phosphating of steel[J].Corrosion Science,1972,12:583.
[4]	Chen Tongyun;Hu Keliang .Preparation and properties of a normal-temperature extra-thin type phosphating solution[J].Corrosion and Protection,2001,22:244.
[5]	Yan Huizhong;Kong Fanqing;Zhao Zengqi et al.Research on phosphating technology of FeCrA1Y material for catalytic support[J].中国稀土学报,2002,20(tk):46.
[6]	朱立群,王建华,刘峰,付宝智.稀土复合作用下常温磷化工艺的研究[J].电镀与涂饰,2001(04):8-13.
[7]	张景双,王家林,杨哲龙,安茂忠,屠振密.含有稀土复合添加剂的中温磷化[J].电镀与环保,2000(05):25-27.
[8]	Kang Cuirong;Meng Qingying;Yang Zhian et al.The electron microstructure analysis of zinc system phosphate coating[J].天津大学学报,1996,29(05):740.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Research on Effect of Rare Earth Compounds in Phosphating Process

参考文献