通过快速凝固和变质处理的综合作用,在铸态铝硅亚共晶合金中原位获得了纤维硅相组织.讨论了各种因素对硅相形态及其演化的影响,重点讨论变质处理对合金组织的改性机制,同时还详细讨论了冷却速率对硅相形态演化的影响.此外,本研究提供了一种制造直纤维增强铝基复合材料的新方法.
The in-situ fibrous Si phase microstructure was obtained in as-cast Al-Si hypoeutectic alloy under the combined effects of rapid solidification and modification. The evolution of Si-phase morphology under such effects was discussed. Focus was based on the modification mechanism of the alloy. Furthermore, the effect of cooling rate on the morphology evolution of Si was discussed. This paper introduced a new approach of fabricating the straight fiber-reinforced Al-based composite.
参考文献
| [1] | Hatch J E.Aluminum:Properties and Physical Metallurgy[M].London:Butterwordth and Co Ltd,1976:346. |
| [2] | Knuutinen A;Nogita K;McDonald S D.[J].Journal of Light Metals,2001(01):229. |
| [3] | Yi Hongkun;Zhang Di .[J].Materials Letters,2003,57:2523. |
| [4] | Xu C L;Wang H Y;Qiu F et al.[J].Materials Science and Engineering A,2006,417:275. |
| [5] | Stuart D. McDonald;Kazuhiro Nogita;Arne K. Dahle .Eutectic nucleation in Al-Si alloys[J].Acta materialia,2004(14):4273-4280. |
| [6] | Sumanth Shankar;Yancy W. Riddle;Makhlouf M. Makhlouf .Nucleation mechanism of the eutectic phases in aluminum-silicon hypoeutectic alloys[J].Acta materialia,2004(15):4447-4460. |
| [7] | Samuel A M;Samuel F H .[J].Journal of Materials Science,1999,31:231. |
| [8] | Dahle A K;Nogita K;McDonald S D et al.[J].Materials Science and Engineering A,2005,413-414:243. |
| [9] | Zhang D L;Cantor B .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24(05):1195. |
| [10] | Lu S Z;Hellawell A .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1987,18(10):1721. |
| [11] | CHRISTIAN J. SIMENSEN;OYVIND NIELSEN;FRANCOIS HILLION .NanoSIMS Analysis of Trace Element Segregation during the Al-Si Eutectic Reaction[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2007(7):1448-1451. |
| [12] | Sebaie E L;Samuel O;Samuel A M et al.[J].Materials Science and Engineering A,2008,480(1-2):342. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%