欢迎登录材料期刊网

材料期刊网

高级检索

针对H62黄铜进行搅拌摩擦焊实验研究,初步分析工艺参数对接头的组织及力学性能的影响.结果表明:当焊接速度与搅拌头旋转速度的比值保持在0.09~0.15之间,压入深度在0.1~0.2 mm之间时,可得到组织致密、无孔洞的搅拌摩擦焊接头;用搅拌摩擦焊得到的黄铜接头的力学性能比母材低,但比熔化焊得到的接头性能要高,其平均抗拉强度可达到母材的88%.

参考文献

[1] 中国焊接学会.焊接手册[M].北京:机械工业出版社,1992
[2] Elrefaey A;Takahashi M;Ikeuchi K.Preliminary investigation of friction stir welding aluminum/copper lap joint[A].Nagoya:Osaka University,2004
[3] Takeshi Shinoda .Recent development of friction stir welding process[J].軽金属溶接,1999(9):406-412.
[4] Kh. A. A. Hassan;A. F. Norman;D. A. Price;P. B. Prangnell .Stability of nugget zone grain structures in high strength Al-alloy friction stir welds during solution treatment[J].Acta materialia,2003(7):1923-1936.
[5] Schneider J A;Nunes A C Jr .Characterization of plastic flow and resulting microtextures in a friction stir weld[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,2004,35:4-13.
[6] 王希靖,郭瑞杰,阿荣,韩晓辉.搅拌摩擦焊接头的温度检测[J].电焊机,2004(01):22-23,54.
[7] Won-Bae Lee;Seung-Boo Jung .The joint properties of copper by friction stir welding[J].Materials Letters,2004(6):1041-1046.
[8] 刘小文,薛朝改,张小剑.铜板搅拌摩擦焊接工艺优化[J].焊接,2003(12):9-12.
[9] 肖兵,柯黎明,王伟兰.紫铜的搅拌摩擦焊接头性能测试与组织分析[J].电焊机,2004(z1):125-129.
[10] 刘小文,鄢君辉,薛朝改,段立宇.铜板搅拌摩擦焊接头金相组织及力学性能[J].焊接学报,2003(06):47-50.
[11] R. W. Fonda;J. F. Bingert;K. J. Colligan .Development of grain structure during friction stir welding[J].Scripta materialia,2004(3):243-248.
[12] Jata K.V.;Semiatin S.L. .Continuous dynamic recrystallization during friction stir welding of high strength aluminum alloys[J].Scripta materialia,2000(8):743-749.
[13] Shibayanagi T;Maeda M.Microstructure and hardness in a joint of 7075 aluminum alloy friction stir welded[A].Nagoya:Osaka University,2004
[14] 周纪华;管克智.金属塑性变形阻力[M].北京:机械工业出版社,1989
[15] Peel M;Steuwer A;Preuss M et al.Microstructure,mechanical properties and residual stresses as a function of welding speed in aluminum AA5083 friction stir welds[J].Acta Materialia,2003,51:4791-4801.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%