采用十二烷基苯磺酸钠(SDBS)作为分散剂,通过超声波作用对纳米SiO2粉体进行水中分散,并采用分散体系粒径分析和测定Zeta 电位及透光率的方法,研究了SDBS含量、超声分散时间等因素对分散性能的影响.结果表明,纳米SiO2的粒径随分散剂含量、超声时间的增加,表现出先减小后缓慢增大的变化趋势.在适量SDBS的条件下,纳米SiO2分散体系因静电和空间位阻的作用而表现出良好的分散稳定性.SDBS对纳米SiO2粉体的较佳分散工艺为:SDBS含量为1.6% ,超声处理时间为18 min.
参考文献
[1] | Jin FY;Chu PK;Tong HH;Zhao J .Improvement of surface porosity and properties of alumina films by incorporation of Fe micrograins in micro-arc oxidation[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(2):863-868. |
[2] | LIAO Haida,ZHANG Lianmeng,WU Bolin.Preparation of Nanosized AlOOH and Its Application in Polymer-inorganic Nanocomposites[J].武汉理工大学学报(材料科学版)(英文版),2008(05):638-643. |
[3] | PENG Bing,HUANG Yi,CHAI Li-yuan,LI Guo-liang,CHENG Ming-ming,ZHANG Xiao-fei.Influence of polymer dispersants on dispersion stability of nano-TiO2 aqueous suspension and its application in inner wall latex paint[J].中南工业大学学报(英文版),2007(04):490-495. |
[4] | HU Yue-hua,QIU Guan-zhou,J.D.Miller.Aggregation/dispersion of ultrafine silica in flotagent solution[J].中国有色金属学会会刊(英文版),2001(05):768-773. |
[5] | 张心亚,沈慧芳,黄洪,蓝仁华,陈焕钦.纳米粒子材料的表面改性及其应用研究进展[J].材料工程,2005(10):58-63. |
[6] | 江成军,段志伟,张振忠,王超.不同表面活性剂对纳米银粉在乙醇中分散性能的影响[J].稀有金属材料与工程,2007(04):724-727. |
[7] | 毛萱,吴佩珠,汤顺清,黄耀熊,唐福星.六偏磷酸钠对纳米羟基磷灰石水中分散行为的影响[J].材料科学与工程学报,2004(05):726-728. |
[8] | 吴敏,程秀萍,葛明桥.纳米SiO2的分散研究[J].纺织学报,2006(04):80-82. |
[9] | 郭兴忠,杨辉,王建武,曹明.聚乙二醇表面改性SiC粉体的物性表征[J].材料工程,2004(03):7-10. |
[10] | 李琰,潘庆谊,陈海华,程知萱,董晓雯.聚乙二醇/纳米氢氧化镍溶胶体系稳定性的研究[J].材料科学与工程学报,2004(02):263-266. |
[11] | 刘吉延,邱骥,索相波.不同分散剂对纳米SiO2水中分散的影响[J].装甲兵工程学院学报,2008(01):80-82. |
[12] | 高健,葛蔚,李静海.浓度对表面活性剂胶团形状影响的分子动力学模拟[J].中国科学B辑,2005(03):252-257. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%