利用扫描电镜观察不同水化环境下粒化高炉矿渣粉水化产物微观形貌,并利用能谱分析水化产物的元素组成,计算水化产物的Ca/Si和Ca/(Si+ Al).试验结果表明:在常温养护条件下,矿渣活性较低,水化产物的Ca/Si、Ca/(Si+ Al)较高;高温养护提高了矿渣的活性,水化产物的Ca/Si、Ca/(Si+ Al)有所降低;常温碱激发环境下矿渣活性得到较好的发挥,矿渣颗粒水化较充分,水化产物的Ca/Si、Ca/(Si+ Al)较低;高温养护碱激发环境下,早期矿渣活性即被激发,但阻碍了后期矿渣活性的发挥.
参考文献
| [1] | Activation Of Algerian Slag In Mortars[J].Construction and Building Materials,2009(1):542-547. |
| [2] | Fathollah Sajedi;Hashim Abdul Razak .Comparison of different methods for activation of ordinary Portland cement-slag mortars[J].Construction and Building Materials,2011(1):30-38. |
| [3] | 崔崇,谢运波,朱守东.少熟料水泥中大掺量矿渣激发条件的研究[J].水泥,2000(02):13-16. |
| [4] | 路青波,杨全兵.影响矿渣潜在活性激发的主要因素研究[J].混凝土与水泥制品,2005(06):13-14. |
| [5] | 袁润章,高琼英,欧阳世翕.矿渣结构与水硬活性及其激发机理[J].武汉工业大学学报,1987(03):297-303. |
| [6] | F. Bellmann;J. Stark .Activation of blast furnace slag by a new method[J].Cement and Concrete Research,2009(8):644-650. |
| [7] | S.Song;H.M.Jenniings .Pore solution chemistry of alkali-activated ground granulated blast-furnace slag[J].Cement and Concrete Research,1999(2):159-170. |
| [8] | S. SONG;D. SOHN;H. M. JENNINGS .Hydration of alkali-activated ground granulated blast furnace slag[J].Journal of Materials Science,2000(1):249-257. |
| [9] | J.I. Escalante-Garcia;J.H. Sharp .The microstructure and mechanical properties of blended cements hydrated at various temperatures[J].Cement and Concrete Research,2001(5):695-702. |
| [10] | S.J. Barnett;M.N. Soutsos;S.G. Millard .Strength development of mortars containing ground granulated blast-furnace slag: Effect of curing temperature and determination of apparent activation energies[J].Cement and Concrete Research,2006(3):434-440. |
| [11] | Fathollah Sajedi .Thermal activation of ordinary Portland cement-slag mortars[J].Materials & design,2010(9):P.4522. |
| [12] | Ekin Altan;Sinan T. Erdogan .Alkali activation of a slag at ambient and elevated temperatures[J].Cement & concrete composites,2012(2):131-139. |
| [13] | 李宇,孙恒虎,赵永宏,王楠.水淬渣的胶凝活性及其形成机理[J].过程工程学报,2007(01):79-84. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%