采用施加超声场来实现AZ80镁合金熔体净化,研究不同功率、不同处理时间及不同静置时间对AZ80镁合金净化的影响.结果表明:超声处理镁合金熔体可以加速熔体中夹杂物的分离,实现熔体的净化.当镁合金熔体在650℃经超声功率80 W,处理时间60 s及静置时间100 s时熔体净化效果最好.铸锭中夹杂物越多电导率越小,电导率可以表征铸锭的净化程度.
参考文献
| [1] | Mordike B L;Ebert T .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2001,A302:37. |
| [2] | I. M. Baghni;WU Yin-shun;LI Jiu-qing .Mechanical properties and potential applications of magnesium alloys[J].Transactions of Nonferrous Metals Society of China,2003(6):1253-1259. |
| [3] | Chen J H;Chen Z H;Yan H G et al.[J].Journal of Alloys and Compounds,2008,461(1-2):209. |
| [4] | Wang Y X;Zeng X Q;Ding W J .[J].Scripta Materialia,2006,54:269. |
| [5] | ZHANG Jing,LI Zhong-sheng,GUO Zheng-xiao,PAN Fu-sheng.Solidification microstructural constituent and its crystallographic morphology of permanent-mould-cast Mg-Zn-Al alloys[J].中国有色金属学会会刊（英文版）,2006(02):452-458. |
| [6] | Schumann S;Friedrich H .[J].Materials Science Forum,2003,51:419. |
| [7] | Bakke P;Pettersen K;Guldberg S.[J].Magnesium Alloys and Their Applications,2000(04):739. |
| [8] | 张军,何良菊,李培杰.镁合金熔体净化工艺的研究[J].铸造,2005(07):665-669. |
| [9] | Xu S X;Shu S S;Mao Y W et al.[J].Foundry,2007,27(01):11. |
| [10] | 黄玉光,吴国华,王玮,侯正全,陈斌,丁文江.熔剂净化对Mg-Gd-Y-Zr合金流动性的影响[J].铸造,2009(02):104-107. |
| [11] | Taniguchi S;Brimacombe J K .[J].ISIJ International,1994,34(09):722. |
| [12] | Kolin A .[J].Science,1953,117(06):134. |
| [13] | 乐启炽,崔建忠,赵晓红.镁合金熔体过滤净化工艺研究[J].特种铸造及有色合金,2005(06):333-334. |
| [14] | Chen F;Huang X;Wang Y.[J].Materials Letters,1998(02):372. |
| [15] | 张志强,乐启炽,崔建忠.高强超声对Mg-Ca合金凝固组织的影响[J].稀有金属材料与工程,2008(03):436-439. |
| [16] | 韩英芬,刘建睿,沈淑娟,黄卫东.镁合金中的非金属夹杂物及其净化方法[J].铸造技术,2006(06):613-616. |
| [17] | 王雪 .[D].沈阳:东北大学,2008. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%