采用超音速火焰喷涂(HVOF)工艺在35钢基体上制备了WC- 10Ni涂层和WC- 12Co涂层,研究了镍、钴这两种粘结剂对WC涂层的显微硬度、摩擦系数和抗磨粒磨损性能的影响,采用扫描电子显微镜观察涂层磨损前后的表面形貌,探讨了WC涂层的磨粒磨损机理.结果表明,以HVOF方法制备的2种WC涂层均有较高的显微硬度,WC- 10Ni涂层和WC- 12Co涂层与SiC砂纸摩擦副之间的干摩擦系数相差不大.2种涂层在低载荷下均有较好的抗磨粒磨损性能,但在较高载荷下WC- 12Co涂层的抗磨性明显优于WC-10Ni涂层.2种涂层的磨粒磨损形式主要为均匀磨耗磨损,磨损机理以微切削和微剥落为主.WC-12Co涂层的磨损表面损伤较轻微,综合性能优于WC- 10Ni涂层.
参考文献
| [1] | 黄智文.谈谈磨粒磨损[J].表面技术,2000(04):34-36. |
| [2] | D.A.Stewart;P.H.Shipway .Microstructural evolution in thermally sprayed WC-Co coatings: comparison between nanocomposite and conventional starting powders[J].Acta materialia,2000(7):1593-1604. |
| [3] | T. Sudaprasert;R. H. Shipway;D. G. McCartney .Sliding wear behaviour of HVOF sprayed WC-Co coatings deposited with both gas-fuelled and liquid-fuelled systems[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(7/12):943-949. |
| [4] | Qiaoqin Yang;Tetsuya Senda;Akira Ohmori .Effect of carbide grain size on microstructure and sliding wear behavior of HVOF-sprayed WC-12% Co coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(1/2):23-34. |
| [5] | WANG Q;CHEN Z H;DING Z X.Performance study of abrasive wear and erosive wear of WC-12Co coatings sprayed by HVOF[A].上海:IEEE,2008:340-344. |
| [6] | Chivavibul P;Watanabe M;Kuroda S;Shinoda K .Effects of carbide size and Co content on the microstructure and mechanical properties of HVOF-sprayed WC-Co coatings[J].Surface & Coatings Technology,2007(3):509-521. |
| [7] | Hawthorne H.M.;Immarigeon J.P.;Legoux J.G.;Parameswaran V.R.;Arsenault B. .Comparison of slurry and dry erosion behaviour of some HVOF thermal sprayed coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(2):825-834. |
| [8] | FERN(A)NDEZ E;CADENAS M;GONZ(A)LEZ R et al.Wear behavior of laser clad NiCrBSi coating[J].Wear,2005,259(7/12):870-875. |
| [9] | 柳春林 .WC-Ni硬质合金研究[J].硬质合金,1997,14(04):211-213. |
| [10] | 黄家明;李维;黄劲松.预弥散强化镍粉——硬质合金的新型粘结剂[J].稀有金属与硬质合金,1999(02):1-3. |
| [11] | 侯岩枫,沈承金,张宏,胡文祥.超音速火焰喷涂锡青铜-钢基双金属材料摩擦性能[J].润滑与密封,2011(01):70-73,84. |
| [12] | 王孝建,王银军.超音速火焰喷涂WC-12Co涂层抗磨粒磨损性能研究[J].热喷涂技术,2010(03):44-48. |
| [13] | 朱子新,徐滨士,马世宁,杜则裕,刘维民.高速电弧喷涂Fe-Al/WC复合涂层的摩擦学特性[J].摩擦学学报,2003(03):174-178. |
| [14] | 简中华,马壮,曹素红,王富耻,王全胜.超音速火焰喷涂WC-Co与NiCr-Cr2C3涂层磨损性能研究[J].材料工程,2007(07):21-24. |
| [15] | Wirojanupatump S.;McCartney DG.;Shipway PH. .The influence of HVOF powder feedstock characteristics on the abrasive wear behaviour of CrxCy-NiCr coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(9):829-837. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%