采用水热电化学法在Ni基体上制备了LiCoO2薄膜.反应温度影响薄膜的择优取向,80℃时制备的薄膜具有(003)取向,100℃制备的LiCoO2薄膜具有(101)和(104)取向,150℃时制备的薄膜取向性不明显.其中以100℃制备的(101)取向LiCoO2薄膜的电化学性能最好,其容量为143mAh/g;10次充放电后,薄膜电极容量衰减小.

LiCoO2 films were fabricated on nickel substrates by a hydrothermal-electrochemical method. The film prepared at 80℃ is mainly (003) plane oriented and prepared at 100℃, (101) and (104) plane oriented and prepared at 150℃ (003) plane oriented as well. The (101) plane orientation is favorable for Li+ diffusion through the cathode, and therefore the (101) plane oriented film contributes to the enhanced electrochemical performance. The film with (101) oriented prepared at 100℃ has the capacity of 143mAh/g and no obvious capacity attenuation detected.

参考文献

[1] Chen C H, Kelder E M, et al. Solid State Ionics, 1996, 86--88 (2): 1301--1306.
[2] Striebel K A, Deng C Z, et al. Journal of the Electrochemical Society, 1996, 143 (6): 1821--1826.
[3] Kim D, Kim M K, et al. Journal of Power Sources, 2002, 108(1--2): 239--244.
[4] Goldner R B, Zerigian P. Materials Research Society Symposium - Proceedings, 1998, 548: 131--136.
[5] Bouwman P J, Boukamp B A, et al. Journal of the Electrochemical Society, 2002, 149 (6): A699--A709.
[6] 石士考, 普玉民. 化学教育, 2000, 7--8: 9.
[7] Cho J, Kim C S, Yoo S I. Electrochemical and Solid-State Letters, 2000, 3 (8): 362--365.
[8] Han K S, Song S W, et al. Electrochemical and Solid-State Letters, 1999, 2 (2): 63--66.
[9] Song S W, Han K S, Yoshimura M, et al. Materials Research Society Symposium - Proceedings, 1999, 606: 205--210.
[10] Yoshimura M. J. Mater. Res., 1998, 13 (4): 796--800.
[11] Tao Ying, et al. Journal of Inorganic Materials, 2003, 18 (2): 500.
[12] 陶颖. 水热电化学法制备LiMO$_2$薄膜电极的机理?研究. 博士学位论文. 长沙: 中南大学, 2004.
[13] 仲维卓, 华素坤. 晶体生长形态学, 第一版. 北京: 科学出版社. 1999.
[14] Bates J B, Dudney N J, Neudecker B J, et al. J. Electrochem Soc., 2000, 147 (1): 59--70.
[15] Hart F X, Bates J B. J. Appl. Phys., 1998, 83 (12): 750--756.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%