研究304奥氏体不锈钢薄板的硬度随冷轧变形量的变化规律，为奥氏体不锈钢薄板工业生产提供指导。同时，采用金相显微镜、维氏硬度测量、x一射线衍射仪和透射电镜研究了不同变形量冷轧对304不锈钢显微组织和机械性能的影响。在室温对0．5mm厚退火板材进行冷轧，使冷轧变形量从10％增加到52％。结果表明，形变诱发马氏体相变是导致304不锈钢冷轧时产生加工硬化的主要原因，冷轧可以显著提高钢的强度和硬度。当冷轧变形至40％时，304不锈钢的维氏硬度是未变形时的2．2倍，屈服强度、抗拉强度分别增大到未变形时的4．2倍（880MPa）和1．8倍（1312MPa）。
To provide a guidance to the industrial production of the austenitic stainless steel sheets, the changing of the cold rolled hardness with the cold rolling reduction of the 304 austenitic stainless steel sheets was investigated. The effect of different thickness reductions by cold rolling on the microstructure and mechanical properties of 304 stainless steels were investigated. The annealed stainless steel sheets were subjected to the cold rolling at room temperature from 10% to 52% thickness reduction. The results indicate that strain-induced martensite transformation clearly results in a significant strengthening of the steel. The hardness and strength of the 304 austenitic stainless steels are improved distinctly. After 40 ~ cold rolling, the Vickers hardness is 2.2 times higher than that of the primary one, the yielding strength and tensile strength are greatly increased to about 880 MPa and 1 312 MPa, respec tively, which are nearly 4.2 times and 1.8 times higher than those of the primary one.
参考文献
| [1] | Ali Hedayati;Abbas Najafizadeh;Ahmad Kermanpur;Farnoosh Forouzan .The effect of cold rolling regime on microstructure and mechanical properties of AISI 304L stainless steel[J].Journal of Materials Processing Technology,2010(8):1017-1022. |
| [2] | Luksza J;Ruminski M;Ratuszek W et al.Texture Evolution and Variations of α-Phase Volume Fraction in Cold-Rolled AISI 301 Steel Strip[J].Journal of Processing Technology,2009,177:555. |
| [3] | Fourlaris G;Gladman T.Microscopical Characterisation of Martensite Formation in a Metasteble Austenitic Stainless Steel[J].Journal of Physics,1997(07):423. |
| [4] | T. S. Byun;N. Hashimoto;K. Farrell .Temperature dependence of strain hardening and plastic instability behaviors in austenitic stainless steels[J].Acta materialia,2004(13):3889-3899. |
| [5] | Maki T.Stainless Steel:Progress in Thermomechanical Treatment[J].Current Opinion in Solid State and Materials Science,1997(02):290. |
| [6] | Padilha A F;Plaut R L;Rios P R .Annealing of Cold-Worked Austenitie Stainless Steels[J].ISIJ International,2003,43:135. |
| [7] | Olsen G B;Cohen M .A mechanism for the Strain-Induced Nucleation of Martensitic Transformation[J].Journal of the Less-Common Metals,1972,28:107. |
| [8] | Olsen G;Cohen M.Kinetics of Strain-Induced Martensite Nucleation[J].Metallurgical and Materials Transactions,1975(6A):791. |
| [9] | Sato K;Ichinose M;Hirotsu Y et al.Effects of Deformation Induced Phase Transformation and Twinning on the Mechanical Properties of Austenitic Fe-Mn-Al Alloys[J].ISIJ International,1989,29:868. |
| [10] | Haugild P;Davydov V;Drahokoupil J et al.Characterization of Strain-induced Martensitic Transformation in a Metastable Austenitic Stainless Steel[J].Materials & Design,2010,31:1821. |
| [11] | 刘伟,李强,焦德志,郑毅,李国平.冷轧301L奥氏体不锈钢的变形和应变硬化行为[J].金属学报,2008(07):775-780. |
| [12] | 刘伟,何俊,周立涛,李国平,陆培德.冷轧奥氏体不锈钢的应变硬化行为及其焊接性能[J].铁道学报,2007(05):117-121. |
| [13] | Murr L E;Staudhammer K P;Hecker S S.Effect of Strain State and Strain Rate on Deformation-Induced Transformation in 304 Stainless Steel,Part Ⅱ[J].Metallurgical and Materials Transactions,1982(A13):627. |
| [14] | Lichtenfeld J A;Mataya N C;Van Tyne C J.Effect of Strain Rate on Stress-Strain Behavior of Alloy 309 and 304L Austenitic Stainless Steel[J].Metal-lurgical and Materials Transactions,2006(37A):147. |
| [15] | Bay B;Hansen N;Hughes D A et al.Evolution of F.C.C.Deformation Structures in Polyslip[J].Acta Metallurgica,1992,40:205. |
| [16] | Di Schino A.;Salvatori I.;Kenny JM. .Effects of martensite formation and austenite reversion on grain refining of AISI 304 stainless steel[J].Journal of Materials Science,2002(21):4561-4565. |
| [17] | Bigdeli Karimi M;Arabi H;Khosravani A et al.Effect of Rolling Strain on Transformation Induced Plasticity of Austenite to Martensite in a High-Alloy Austenitic Steel[J].Journal of Processing Technology,2008,203:349. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%