采用高温熔炼方法后机械球磨和机械合金化方法分别制备了CoFe3Sb12和FeSb2合金粉末,并对其电化学嵌锂性能进行了研究.研究发现,FeSb2的首次可逆容量为394 mAh·g-1,比CoFe3Sb12的首次可逆容量(485 mAh·g-1)低.但是FeSb2容量衰减的速度要远远小于CoFe3Sb12.FeSb2的容量保持率在第10个循环时仍保持在70%以上,而 CoFe3Sb12却只有50%左右.通过二者嵌锂性能对比研究表明,减少嵌锂活性中心能有效地缓解合金类负极材料在循环中的容量衰减现象.
参考文献
| [1] | Flandrois S.;Simon B. .Carbon meterials for lithium-ion rechargeable batteries[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(2):165-180. |
| [2] | Yoshio Idota;Tadahiko Kabota .[J].科学,1997,276:1395. |
| [3] | Ian A Courney;Mckinnon W R .[J].Journal of the Electrochemical Society,1999,146:59. |
| [4] | Bourderau S;Brousse T;Schleich D M .[J].Journal of Power Sources,1999,81-82:233. |
| [5] | Zhang X W;Wang C S;Appleby A J;Little F E .[J].Journal of Power Sources,2002,109:136. |
| [6] | Jong G J;Kim Y U;Sohn H J;Kang T .[J].Journal of Power Sources,2001,101:201. |
| [7] | 曹高劭,赵新兵.金属Sb与石墨复合材料的电化学吸放锂性质[J].稀有金属材料与工程,2003(11):915-918. |
| [8] | Zhao X B;Cao G S;Lü C P;Zhang L J .[J].Journal of Alloys and Compounds,2001,315:265. |
| [9] | Mao O;Dunlap R A;Dahn J R .[J].Journal of the Electrochemical Society,1999,146:405. |
| [10] | 张丽娟,赵新兵,蒋小兵,吕春萍.金属间化合物CoSb3的电化学嵌锂特性研究[J].稀有金属材料与工程,2001(04):268-272. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%