研究了以砖粉、粉煤灰和矿渣粉为主要原料开发的BSF复合粉体作为矿物掺合料对混凝土干燥收缩的影响，以及三种原料分别对混凝土干燥收缩的作用机理。试验结果表明粘土砖粉和粉煤灰能小幅的补偿收缩，并且随着其掺量的增加，混凝土收缩减少的幅度也增大；而矿渣粉的掺入会加剧混凝土收缩， BSF复合粉体对混凝土体积稳定性的影响与三种原料的相互作用有关，混凝土中10 nm以下的微孔对干缩的影响最大。
The shrinkage performance of C 35 pavement concrete with BSF admixture , the influence of BSF admixture on the shrinkage of concrete as well as the effect mechanism of brick powder , fly ash and granulated blast furnace slag ( GBFS) powder on the shrinkage of concrete were investigated .The results showed that:clay brick powder and fly ash could compensate the shrinkage of concrete slightly , and with the increase of dosage of these two kind of materials , the drop amplitude of concrete shrinkage rate increased.On the contrary, GBFS powder could aggravate the shrinkage of concrete .The shrinkage performance of C35 pavement concrete was attributed to the interaction of brick powder , fly ash and GBFS, composite admixture .For the concrete shrinkage , the microhole smaller than 10 nm played dominate role .
参考文献
| [1] | 周文娟;陈家珑;路宏波.我国建筑垃圾资源化现状及对策[J].建筑技术,2009(8):741-744. |
| [2] | 王雪;孙可伟.废砖资源化综合利用研究[J].中国资源综合利用,2008(10):34-35. |
| [3] | 李辉;苏媛婷;张浩.西安市建筑垃圾的基本性质研究[J].硅酸盐通报,2015(3):853-858. |
| [4] | 柯南生.浅析水泥混凝土路面破坏开裂的原因[J].公路交通科技·应用技术版,2011(2):61-63. |
| [5] | 王涛.混凝土早期收缩、开裂的原因以及提高耐久性的措施[J].科技与创新,2014(17):80-80,82. |
| [6] | 段小芳;刘海涛;乔勤勤.混凝土早期收缩研究现状[J].山西建筑,2014(27):122-123. |
| [7] | G. Appa Rao.Long-term drying shrinkage of mortar - influence of silica fume and size of fine aggregate[J].Cement and Concrete Research,20012(2):171-175. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%