By means of surface mechanical attrition treatment (SMAT), the grain size with a diameter of about 60nm formed at about 20μm depth and numerous mechanical twins at about 50μm depth from the treated surface were synthesized in 316L stainless steel because of the different distributions of strain and strain rate along depth orientation. For instance the maximum strain rate reached103-104s-1 on the top surface. The relationship between the microstructure and the corrosion property was studied in 0. 05M H2SO4+ 0.25M Na2SO4 aqueous solution, and the results show an extreme improvement of corrosion resistance owing to the appearance of twin boundaries and the obvious reduction in corrosion resistance attributed to the presence of nanocrystaline boundaries.
参考文献
| [1] | K.Lu;J.Lu,J .[J].mater Sci Technol,1999,15:193. |
| [2] | G.Liu;J.Lu;K.Lu .[J].Mater Sci Eng,200,A286:91. |
| [3] | N. R. Tao;Z. B. Wang;W. P. Tong;M. L. Sui;J. Lu;K. Lu .An investigation of surface nanocrystallization mechanism in Fe induced by surface mechanical attrition treatment[J].Acta materialia,2002(18):4603-4616. |
| [4] | Z.B. Wang;N.R. Tao;S. Li .Effect of surface nanocrystallization on friction and wear properties in low carbon steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):144-149. |
| [5] | X.Wu;N. Tao;Y. Hong .Microstructure and evolution of mechanically-induced ultrafine grain in surface layer of AL-alloy subjected to USSP[J].Acta materialia,2002(8):2075-2084. |
| [6] | S.H.Kim;K.T.Aust;U.Erb;F.Gonzalez and G .[J].Palumbo Scripta Mater,2003,48:1379. |
| [7] | G.Palumbo;F.Gonzalez;A.M.Brennenstuhl;U.Erb,W.Shmayda and P.C.Lichtenberger .[J].Nanostruct Mater,1997,9:737. |
| [8] | W.Zeiger;M.Schneider;D.Scharnweber;H.Worth .[J].Nanostructur Mater,1995,6:1013. |
| [9] | G.Palumbo;K.T.Aust .[J].Acta Metall Mater,1990,38:2343. |
| [10] | P.Lin;G.Palumbo;U.Erb;K.T.Aust .[J].Scripta Metal Mater,1995,33:387. |
| [11] | E. M. Lehockey;G. Palumbo;P. Lin;A. M. Brennenstuhl .ON THE RELATIONSfflP BETWEEN GRAIN BOUNDARY CHARACTER DISTRIBUTION AND INTERGRANULAR CORROSION[J].Scripta materialia,1997(10):1211-1218. |
| [12] | E.A.Trillo;L.E.Murr .[J].Acta Mater,1999,47:235. |
| [13] | W.P.Tong;N.R.Tao;Z.B.Wang;J.Lu and K.Lu .[J].Science,2003,299:686. |
| [14] | G.B.Olson;M.Cohen .[J].Metall Trans,1975,6A:791. |
| [15] | T.M.Devine;C.L.Briant;B.J.Drummond .[J].Scripta Metallurgica,1980,14:1175. |
| [16] | C. Suryanarayana .Nanocrystalline materials[J].International Materials Reviews,1995(2):41-64. |
| [17] | E.A.Abd e1Meguid;N.A.Mahmoud;V.K.Gouda .[J].British Corrosion Journal,1998,33:42. |
| [18] | A.Barbucci;G.Farne;P.Matteazzi;R.Riccieri and G.Cerisola .[J].Corrosion Science,1999,3:463. |
| [19] | T.Watanabe .[J].Research Mechanica,1984,11:47. |
| [20] | E.M.Lehockey;G.Palumbo;P.Lin .[J].Scripta Mater,1998,40:50. |
| [21] | C.Cheung;U.Erb;G.Palumbo .[J].Mater Sci Eng,1994,A185:39. |
| [22] | H. W. Zhang;Z. K. Hei;G. Liu;J. Lu;K. Lu .Formation of nanostructured surface layer on AISI 304 stainless steel by means of surface mechanical attrition treatment[J].Acta materialia,2003(7):1871-1881. |
| [23] | G. Palumbo;E. M. Lehockey;P. Lin .Applications for grain boundary engineered materials[J].JOM,1998(2):40-43. |
| [24] | X.R.Qian;Y.T.Chou .[J].Phil Mag,1982,A45:1075. |
| [25] | U.Erb;H.Gleiter;G.Schwitzgebel .[J].Acta Metall,1982,30:1377. |
| [26] | Y.B.Hong;K.Hiroyuki;J.W.Zhan;S.Masayuki and S.S.Yutaka .[J].Scripta Mater,2003,49:219. |
| [27] | P.H.Pumphrey;H.Gleiter .[J].Phil Mag,1974,30:593. |
| [28] | H.Kokawa;T.Watanabe;A.Vehara;S.Karashima .[J].Scripta Metall,1978,12:357. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%