利用透射电镜(TEM)中的原位拉伸台对纯金属铝及受强度错配双界面约束的纯铝层拉伸过程进行观察.结果表明:纯金属铝拉伸过程中裂端形成微孔洞后即与主裂纹连接,在界面约束条件下,裂端形成微孔后并非立即与主裂纹连通,而是在更前沿位置产生更多的微孔洞,即发生连续孔洞化.拉伸过程中,裂尖钝化与锐化的现象共存,随着中间纯铝层厚度的降低,裂端发射的位错在其周围晶界形成越来越严重的塞积,大大提高了晶界及裂端前沿应力场强度,引起中间纯铝层的脆化.
参考文献
| [1] | Tvergaard V;Huang Y;Huchinson W.[J].Journal of Eur J Mech A Solids:215. |
| [2] | Cox T B;Low J R.[J].Metallurgical and Materials Transactions:1457. |
| [3] | Thomson R D .[J].International Journal of Fracture,1984,26(02):99. |
| [4] | Reimanis I E;Dalgleish B J.[J].Acta Metallurgica et Materialia:2645. |
| [5] | Kassner M E;Kennedy T C;Schrems K K.[J].Acta Materialia,1998(18):6445. |
| [6] | Sun J.[J].Chinese Journal of Mechanical Engineering,1991:14. |
| [7] | KwonD;Asaro R J.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science:117. |
| [8] | Ashby M F;Blunt F J;Bannister M.[J].Acta Materialia,1989(07):1847. |
| [9] | Hsia K J;Suo Z;Yang W.[J].Journal of the Mechanics and Physics of Solids(06):877. |
| [10] | 韩礼红,李梁,孙军.双界面约束下纯铝层韧脆转变行为的实验研究[J].金属学报,2003(09):920-925. |
| [11] | Reimanis I E;Dalgleish B J;Evans A G.[J].Acta Metallurgica et Materialia:3133. |
| [12] | 潘金生;仝健民;田民波.材料科学基础[M].北京:清华大学出版社,1998:178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%