Orthorhombic LiMnO2 cathode materials were synthesized successfully at lower temperature by sol-gel method. When LiMnO2 precursor prepared by sol-gel method was fired in air, the product was a mixture of spinel structure LiMn2O4and rock-salt structure Li2MnO3, whereas in argon single-phase orthorhombic LiMnO2 could obtain at the range of 750℃ to 920℃. The substitution of Mn by Zn2+ or Co3+ in LiMnO2 led to the structure of LiMnO2 transiting to α-LiFeO2. The results of electrochemical cycles indicated that the discharged capacity of orthorhombic-LiMnO2was smaller at the initial stages, then gradually increased with the increasing of cycle number, finally the capacity stabilized to certain value after about 10th cycles. This phenomenon reveals that there is an activation process for orthorhombic LiMnO2 cathode materials during electrochemical cycles, which is a phase transition process from orthorhombic LiMnO2 to tetragonal spinel Li2Mn2O4. The capacity of orthorhombic LiMnO2 synthesized at lower temperature is larger than that synthesized at high temperature.
参考文献
| [1] | J.J.Davision;R.S.McMillan;J.J.Murray;J.E.Greedan .[J].Journal of Power Sources,1995,54:232. |
| [2] | I. M. Kotschau;J. R. Dahn .In situ X-ray study of LiMnO{sub}2[J].Journal of the Electrochemical Society,1998(8):2672-2677. |
| [3] | E Lelvi;E Zinigrad;H Teller;M D Levi D Aurbach .[J].Journal of the Electrochemical Society,1998,145(10):3440. |
| [4] | YoungllJang;Biying Huang;Haifeng Wang;Donald R Sadoway and Yetming Chiang .[J].Journal of the Electrochemical Society,1999,146(09):3217. |
| [5] | G X Wang;Sun S Zhong;P Yao;D H Bradhurst S X Dou and H K Liu.[J].Journal of New Materials Systems,1999(02):215. |
| [6] | YoungllJang;Yetming Chiang .[J].Solid State Ionics,2000,130:53. |
| [7] | A R Armstrong;P G Bruce .[J].Nature,1996,381(06):499. |
| [8] | M Tauchi;K Ado H Kobayashi;H Kageyama .[J].Journal of the Electrochemical Society,1998,145(04):L49. |
| [9] | Ammundsen;J Desilvestro;T Groutso;D Hassell,J B Metson,E Regan,R Steiner,and P J Pickering .[J].Journal of the Electrochemical Society,2000,147(11):4078. |
| [10] | J. M. Paulsen;C. L. Thomas;J. R. Dahn .Layered Li-Mn-oxide with the 02 structure: a cathode material for Li-Ion cells which does not convert to spinel[J].Journal of the Electrochemical Society,1999(10):3560-3565. |
| [11] | G.Ceder;S.K.Mishra .The Stability of Orthorhombic and Monoclinic-Layered LiMnO2[J].Electrochemical and solid-state letters,1999(11):550-552. |
| [12] | R Hoppe;G Brachtel;M Jansen.[J].Z:Anorg:Allg:Chem,1975(01):417. |
| [13] | K. Katayama;H. Kamiyama;Y. Azuma .Preparation af Single-Phase Lithium Manganates[J].Key engineering materials,1999(157/158):281-288. |
| [14] | M Yoshio;S Inoue;M Hyakutake;G.Piao and H.Nakamura .[J].Journal of Power Sources,1991,34:147. |
| [15] | E Lelvi;E Zinigrad;H Teller;M D Levi and D Aurbach .[J].Journal of the Electrochemical Society,1998,145(10):3440. |
| [16] | H Nakamura;K Motooka;H Noguchi;M.Yoshio .[J].Journal of Power Sources,1999,81-82:632. |
| [17] | Y Nitta;M Nagayama;H Miyake;A Ohta .[J].Journal of Power Sources,1999,81-82:49. |
| [18] | E J Wu;P D Tepesch;G Ceder .[J].PHILOSOPHICAL MAGAZINE B-PHYSICS OF CONDENSED MATTER STATISTICAL MECHANIC,1998,77:1039. |
| [19] | L Croguennec;P Deniard;R Brec .[J].Journal of the Electrochemical Society,1997,144(10):3323. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%