Vertical ZnO nanotube （ZNT） arrays were synthesized onto an indium doped tin oxide （ITO） glass substrate by a simple electrochemical deposition technique followed by a selective etching process. Scanning electron microscopy （SEM） showed formation of well-faceted hexagonal ZNT arrays spreading uniformly over a large area. X-ray diffraction （XRD） of ZNT layer showed substantially higher intensity for the （0002） diffraction peak, indicating that the ZnO crystallites were well aligned with their c-axis. Profilometer measurements of the ZNT layer showed an average thickness of -7 μm. Diameter size distribution （DSD） analysis showed that ZNTs exhibited a narrow diameter size distribution in the range of 65-120 nm and centered at -75 nm. The photoluminescence （PL） spectrum measurement showed violet and blue luminescence peaks that were centered at 410 and 480 nm, respectively, indicating the presence of internal defects. Ultra-violet （UV） spectroscopy showed major absorbance peak at ,-348 nm, exhibiting an increase in energy gap value of 3.4 eV. By employing the formed ZNTs as the photo-anode for a dye-sensitized solar cell （DSSC）, a full-sun conversion efficiency of 1.01% was achieved with a fill factor of 54%. Quantum efficiency studies showed the maximum of incident photon-to-electron conversion efficiency in a visible region located at 590-550 nm range.