筛选出了催化性能较好的活性炭负载氯化钙（CaCl2/AC）催化剂用于五氯乙烷脱HCl制备四氯乙烯。考察了反应温度、空速、CaCl2负载量对CaCl2/AC催化剂催化性能的影响及催化剂的稳定性。实验结果表明最佳反应条件：反应温度为240℃,空速为3.4h-1,CaCl2负载量为0.3mmol/g,在此反应条件下五氯乙烷的转化率可达99%以上,四氯乙烯的收率达95%以上,催化剂催化性能重现性良好。采用X射线衍射（XRD）、氮气吸附-脱附对催化剂进行了表征。结果表明CaCl2在活性炭表面分散良好;随着CaCl2负载量的增加,CaCl2/AC催化剂的BET比表面及孔容逐渐减小。
Supported catalyst calcium chloride/activated carbon（CaCl2/AC） was prepared and used in dehydrochlorination of pentachloroethane to produce perchloroethylene.Influences of reaction temperature,space velocity and CaCl2 loading amount on catalytic activity of CaCl2/AC were investigated.Stability of catalytic activity of catalyst was also studied.Results of the experiment showed that the optimal conditions were reaction temperature 240℃,space velocity 3.4h-1,CaCl2 loading amount 0.3mmol/g.Under the optimal conditions,the conversion of pentachloroethane and the yield of perchloroethylene can reach more than 99% and 95%,respectively.And the repeatability of catalytic activity of catalyst was fine.The catalysts were characterized by X-ray diffraction（XRD） and nitrogen adsorption-desorption method.The results showed that the dispersion of CaCl2 on activated carbon surface was good.The BET surface area and pore volume of CaCl2/AC catalyst gradually decreased with the CaCl2 loading amount increased.
参考文献
| [1] | Fukami N;Yosida M;Lee B D et al.[J].Chemosphere,2001,42(04):345-350. |
| [2] | Huggins F E;Vaidya S V;Shah N et al.[J].Fuel Pro- cessing Technology,1993,35(03):233-257. |
| [3] | Doherty R E .[J].Environmental Forensics,2000,1(02):69-81. |
| [4] | 费平.光催化合成五氯乙烷的研究[J].氯碱工业,2011(01):30-34. |
| [5] | Seiler W U .[J].Chemical and Engineering News,1960,38(22):124-129. |
| [6] | 商超平,张艳梅,沈晔.国内外四氯乙烯生产消费现状及市场前景[J].中国氯碱,2006(03):4-7. |
| [7] | Cervini-Silva J;Larson R A;Wu J et al.[J].Chemo- sphere,2002,47(09):971-976. |
| [8] | Cervini-Silva J;Kostka J E;Larson R A et al.[J].Envi- ronmental Toxicology and Chemistry,2003,22(05):1046-1050. |
| [9] | 赵红坤;张道森;李嵘嵘 等.[P].中国专利:CN101032690A,2007-09-12. |
| [10] | Wang D L;Chen M M;Wang C Y et al.[J].Materials Letters,2011,65(07):1069-1072. |
| [11] | 沈曾民;张文辉;张学军.活性炭材料的制备与应用[M].北京:化学工业出版社,2006:194-195. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%