采用湿化学共沉淀法合成羟基磷灰石(HAp),以明胶作为表面包覆改性剂,在反应温度为90℃,溶液pH值为8的条件下获得了纳米HAp颗粒,分析了HAp形核、生长机理以及工艺参数对产物粒度、颗粒形貌及结晶度的影响,制备出了高长径比的纳米棒状HAp,解决了合成温度高导致的HAp尺寸偏大,长径比小的问题.结果表明,明胶分子不但对HAp晶体的生长有明显的控制作用,而且对HAp纳米晶体的微观分布也产生影响,可使HAp形成高度取向的簇状分布.
参考文献
| [1] | Yeong K C B;Wang J;Ng S C .[J].Biomaterials,2001,22:2705. |
| [2] | Suchanek W.;Yoshimura M. .Processing and properties of hydroxyapatite-based biomaterials for use as hard tissue replacement implants [Review][J].Journal of Materials Research,1998(1):94-117. |
| [3] | Fujishiro Y;Yabuki H;Kawamura K et al.[J].Journal of Chem Tech Biotechnology,1993,57:349. |
| [4] | Layrolle P.;Tateishi T.;Ito A. .Sol-gel synthesis of amorphous calcium phosphate and sintering into microporous hydroxyapatite bioceramics[J].Journal of the American Ceramic Society,1998(6):1421-1428. |
| [5] | Liu Changsheng;Huang Yue;Shen Wei et al.[J].Biomaterials,2001,22:301. |
| [6] | 廖其龙,徐光亮,周大利,尹光福,郑昌琼,李晓东.水热合成纳米羟基磷灰石粉末及其结构表征[J].四川大学学报(工程科学版),2002(03):69-71. |
| [7] | Chen CW;Riman RE;TenHuisen KS;Brown K .Mechanochemical-hydrothermal synthesis of hydroxyapatite from nonionic surfactant emulsion precursors[J].Journal of Crystal Growth,2004(3/4):615-623. |
| [8] | 宋云京,李木森,温树林,李士同,敖青,李胜利,伦宁.工艺参数对羟基磷灰石沉淀形态和相结构的影响[J].电子显微学报,2002(05):695-696. |
| [9] | 宋云京,李木森,温树林,姜庆辉,宿庆财.温度和pH值对羟基磷灰石粉体合成的影响[J].硅酸盐通报,2003(02):7-10. |
| [10] | 郭连峰,张文光,王成焘.Ca10（PO4）6（OH）2纳米粉体的制备及TEM分析[J].电子显微学报,2004(03):234-237. |
| [11] | 王德平,王璐,黄文旵.pH值对化学沉淀法制备纳米羟基磷灰石的影响[J].同济大学学报（自然科学版）,2005(01):93-98. |
| [12] | 荣国斌.波谱数据表-有机化合物的结构解析[M].上海:华东理工大学出版社,2004:306. |
| [13] | Chang MC;Ko CC;Douglas WH .Preparation of hydroxyapatite-gelatin nanocomposite.[J].Biomaterials,2003(17):2853-2862. |
| [14] | Kozue Furuichi;Yuya Oaki;Hiroaki Imai .[J].Chemistry of Materials,2006,18(01):229. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%